Wellamid® GF1685-WBK1
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Wellman Engineering Resins |
| Trademark: | Wellamid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | OVuweg_Wellamid-GF1685-WBK1.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Wellamid® GF1685-WBK1 is a Polyamide 6 (Nylon 6) material filled with 20% glass fiber. It is available in Asia Pacific, Europe, Latin America, or North America for injection molding. Typical application of Wellamid® GF1685-WBK1: Automotive |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.28 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow : 23°C | 0.70 to 1.1 | % | |
| Flow : 23°C | 0.30 to 0.70 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield, 23°C) | 145 | MPa | ISO 527-2 |
| Tensile Strain (Yield, 23°C) | 3.0 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 6300 | MPa | ISO 178 |
| Flexural Stress (23°C) | 205 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength (23°C) | 6.0 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 205 | °C | ISO 75-2/A |
| Melting Temperature (DSC) | 220 | °C | ISO 3146 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 79.4 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 260 to 282 | °C | |
| Middle Temperature | 254 to 277 | °C | |
| Front Temperature | 249 to 271 | °C | |
| Nozzle Temperature | 249 to 271 | °C | |
| Processing (Melt) Temp | 254 to 282 | °C | |
| Mold Temperature | 65.6 to 93.3 | °C | |
| Injection Pressure | 34.5 to 138 | MPa | |
| Back Pressure | 0.345 | MPa | |
| Screw Speed | 30 to 120 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shuang-Bang WU-6100RP | Shuang-Bang Industrial Corp. | PUR, Unspecified | Shuang-Bang |
| Zhongfa PP pp9 | Yuyao Zhongfa Engineering Plastics Co. Ltd. | PP, Unspecified | Zhongfa |
| Ferro PP WPP20SD05NA | Ferro Corporation | PP Homopolymer | Ferro PP |
| KMI KM KB ABS | KMI Group, Inc. | ABS | KMI |
| LNP™ LUBRICOMP™ QCP36 compound | SABIC Innovative Plastics | Nylon 610 | LNP™ LUBRICOMP™ |