RIGITRON 10001
| Category: | PC , Polycarbonate |
| Manufacturer: | Ovation Polymers Inc. |
| Trademark: | RIGITRON |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | OVPmCB_RIGITRON-10001.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PC - Impact Modified, high tensile strength, stiffness and HDT. |
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.19 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 17 | g/10 min | ASTM D1238 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 3.17 mm | 0.20 to 0.40 | % | |
| Across Flow : 3.17 mm | 0.10 to 0.40 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 1850 | MPa | ASTM D638 |
| Tensile Strength 2(Yield) | 64.0 | MPa | ASTM D638 |
| Tensile Elongation 3(Break) | 20 | % | ASTM D638 |
| Flexural Modulus 4 | 2250 | MPa | ASTM D790 |
| Flexural Strength 5(Yield) | 90.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 690 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Annealed, 3.20 mm) | 125 | °C | ASTM D648 |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® F02-081A-10C | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| Moplen EP201N | LyondellBasell Industries | PP Impact Copolymer | Moplen |
| Diamond ABS 7500E | Network Polymers, Inc. | ABS | Diamond ABS |
| Fainplast PVC RL 715/3 | Fainplast Compounds S.r.l | PVC, Rigid | Fainplast PVC |
| PERLAS® O07F4000B00 | A.D. Compound S.p.A. | PP Homopolymer | PERLAS® |