Ultramid® A3UG5
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | BASF Corporation |
| Trademark: | Ultramid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | OVNuFi_Ultramid-A3UG5.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Without halogenes and red phosphorus a flame retarded glass fiber reinforced injection moulding grade; light in colour with outstanding mechanical and electrical properties. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.39 | -- | g/cm³ | ISO 1183 |
| Apparent Density | 0.70 | -- | g/cm³ | |
| Melt Volume-Flow Rate (MVR) (275°C/5.0 kg) | 25.0 | -- | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 1.2 | -- | % | |
| Flow | 0.40 | -- | % | |
| Water Absorption | ISO 62 | |||
| Saturation, 23°C | 4.0 to 4.6 | -- | % | |
| Equilibrium, 23°C, 50% RH | 1.1 to 1.5 | -- | % | |
| Viscosity Number (96% H2SO4 (Sulphuric Acid)) | 165 | -- | cm³/g | ISO 307 |
| Mold Shrinkage - model-housing (1.50 mm) | 0.40 | -- | % |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Temperature Index - at 50% loss of tensile strength | IEC 60216 | |||
| -- 1 | 155 | -- | °C | |
| -- 2 | 130 | -- | °C |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Fire Performance - UL94+HAI+HWI 3 | > 750.0 | -- | µm | UL 746C |
| French Railway Standard - Fire and smoke classification 4 | I3/F2 | -- | NF F16-101 | |
| Smoke Density - Ds max. (20 min), 25kW/m² (2.00 mm) | 250 | -- | ISO 5659-2 | |
| Smoke Toxicity 5 | 0.380 | -- |
| Additional Information | Dry | Conditioned | ||
|---|---|---|---|---|
| Polymer Abbreviation | PA66-GF25 FR | -- |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 9500 | 6100 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 145 | 90.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 3.0 | 5.0 | % | ISO 527-2 |
| Flexural Modulus | 9500 | 6100 | MPa | ISO 178 |
| Flexural Stress | 230 | 160 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 7.5 | 9.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 63 | -- | kJ/m² | |
| 23°C | 65 | 65 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 260 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 245 | -- | °C | ISO 75-2/A |
| Melting Temperature | 260 | -- | °C | ISO 11357-3 |
| RTI Elec (1.50 mm) | 120 | -- | °C | UL 746 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | -- | 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+16 | 1.0E+13 | ohms·cm | IEC 60093 |
| Relative Permittivity (1 MHz) | 3.80 | 4.60 | IEC 60250 | |
| Dissipation Factor (1 MHz) | 0.017 | 0.10 | IEC 60250 | |
| Comparative Tracking Index (Solution A) | 600 | -- | V | IEC 60112 |
| High Amp Arc Ignition (HAI) (> 0.750 mm) | PLC 0 | -- | UL 746 | |
| Hot-wire Ignition (HWI) 6(> 0.750 mm) | PLC 0 | -- | UL 746 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| > 0.750 mm | V-0 | -- | ||
| 1.60 mm | V-0 | -- | ||
| 3.20 mm | V-0 | -- | ||
| Glow Wire Flammability Index (0.750 mm) | 960 | -- | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature (> 2.00 mm) | 775 | -- | °C | IEC 60695-2-13 |
| Oxygen Index | 32 | -- | % | ISO 4589-2 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 280 to 300 | °C | |
| Mold Temperature | 80.0 to 90.0 | °C |
| Note Message | |
|---|---|
| 1 . | 5000 h |
| 2 . | 20000 h |
| 3 . | For Electrical Insulation/Barrier with close proximity (<0.8 mm) to unisulated live parts according to UL 746C |
| 4 . | Limited validity period |
| 5 . | NF X70-100-1/-2 |
| 6 . | ASTM D3874-88 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RheTech Polypropylene G13P100-01UV | RheTech, Inc. | PP, Unspecified | RheTech Polypropylene |
| TECHNYL® A 218 S30 BLACK 21 N | Solvay Engineering Plastics | Nylon 66 | TECHNYL® A |
| LUVOCOM® 1301-8148 | Lehmann & Voss & Co. | PPS | LUVOCOM® |
| Sylvin 6411-92 Black | Sylvin Technologies Incorporated | CPE | Sylvin |
| NORYL™ NHP9023 resin | SABIC Innovative Plastics Asia Pacific | PPE | NORYL™ |