Innothane® IE-3080
| Category: | TSU , Polyurethane Thermoset Elastomer |
| Manufacturer: | Innovative Polymers, Inc. |
| Trademark: | Innothane® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | OVM2B7_Innothane-IE-3080.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| IE-3080 is a rigid polyurethane formulated for room temperature hand-batch or vacuum assisted casting methods. Excellent physical properties can be obtained with a room temperature cure without the utilization of mercury, MOCA or TDI. IE-3080 has a very low mixed viscosity. It is ideal for color-matching due to its neutral semi-transparent appearance. |
| General Information | |
|---|---|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| Hardener | 1.03 | g/cm³ | |
| Cured | 1.08 | g/cm³ | |
| Base Resin | 1.10 | g/cm³ | |
| Molding Shrinkage - Flow | 0.50 to 1.0 | % | ASTM D2566 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus | 1380 | MPa | ASTM D790 |
| Flexural Strength | 53.8 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 32 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 60.0 | °C | |
| 1.8 MPa, Unannealed | 55.0 | °C |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Hardener | Mix Ratio by Volume: 100 Mix Ratio by Weight: 94 | ||
| Resin | Mix Ratio by Weight: 100 Mix Ratio by Volume: 100 | ||
| Demold Time | 45 to 75 | min |
| Uncured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Viscosity | |||
| 25°C 1 | 0.040 | Pa·s | |
| 25°C 2 | 0.10 | Pa·s | |
| 25°C 3 | 0.25 | Pa·s | |
| Curing Time (25°C) | 1.7E+2 | hr | |
| Gel Time | 7.0 to 9.0 | min |
| Cured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 65 to 75 | ASTM D2240 | |
| Tensile Strength | 31.0 | MPa | ASTM D638 |
| Tensile Elongation at Break | 11 | % | ASTM D638 |
| Note Message | |
|---|---|
| 1 . | Resin |
| 2 . | Mixed |
| 3 . | Hardener |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Santoprene™ 8211-75 | ExxonMobil Chemical | TPV | Santoprene™ |
| Bakelite® PF 2400 | Hexion Inc. | Phenolic | Bakelite® |
| Geon™ 130 Series 137 | Mexichem Specialty Resins, Inc. | PVC Copolymer | Geon™ 130 Series |
| Karina BLACK PVC COMPOUND 880-48/ 1-E-AC | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Hostacom PPU X9067HS C12507 | LyondellBasell Industries | PP Copolymer | Hostacom |