Laril 13 G/20
| Category: | PPE+PS , Polyphenylene Ether + PS |
| Manufacturer: | LATI S.p.A. |
| Trademark: | Laril |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | OSBAKI_Laril-13-G-20.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Compound based on Modified Polyphenylene Oxyde (PPOm). Glass fibres. Low thermal expansion coefficient. Good thermal resistance. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.22 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | ISO 294-4 | ||
| Across Flow : 2.00 mm | 0.50 to 0.70 | % | |
| Flow : 2.00 mm | 0.40 to 0.65 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | ISO 527-2/1 | ||
| 23°C | 6300 | MPa | |
| 60°C | 6300 | MPa | |
| 90°C | 5800 | MPa | |
| 120°C | 4200 | MPa | |
| Tensile Stress | ISO 527-2/5 | ||
| Yield, 60°C | 60.0 | MPa | |
| Yield, 90°C | 45.0 | MPa | |
| Yield, 120°C | 30.0 | MPa | |
| Break, 23°C | 80.0 | MPa | |
| Break, 60°C | 60.0 | MPa | |
| Break, 90°C | 45.0 | MPa | |
| Break, 120°C | 25.0 | MPa | |
| Tensile Strain | ISO 527-2/5 | ||
| Yield, 60°C | 2.0 | % | |
| Yield, 90°C | 1.8 | % | |
| Yield, 120°C | 1.7 | % | |
| Break, 23°C | 2.5 | % | |
| Break, 60°C | 2.5 | % | |
| Break, 90°C | 2.5 | % | |
| Break, 120°C | 4.0 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -20°C | 5.0 | kJ/m² | |
| 23°C | 6.0 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -20°C | 25 | kJ/m² | |
| 23°C | 25 | kJ/m² | |
| Notched Izod Impact (23°C, 3.20 mm) | 80 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 135 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 125 | °C | ISO 75-2/A |
| Continuous Use Temperature 2 | 120 | °C | |
| Vicat Softening Temperature | 140 | °C | ISO 306/B50 |
| CLTE - Flow (30 to 100°C) | 3.0E-6 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index 3(Solution A) | 225 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxygen Index | 25 | % | ASTM D2863 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 90.0 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 270 to 290 | °C | |
| Mold Temperature | 80.0 to 90.0 | °C | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | at 60 Mpa of cavity pressure |
| 2 . | 20,000 hr |
| 3 . | Without Surfactant |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TECHLEN M7462 | DAEHA Co., LTD | PP, Unspecified | TECHLEN |
| SureSpec HP-040 | Genesis Polymers | PP, HMS | SureSpec |
| ELASTOSIL® LR 3015/70 A/B | Wacker Chemie AG | Silicone | ELASTOSIL® LR |
| LNP™ VERTON™ RV00CEXS compound | SABIC Innovative Plastics | Nylon 66 | LNP™ VERTON™ |
| Durez® 33171 | SBHPP | Phenolic | Durez® |