ATTANE™ SL 4102G
| Category: | ULDPE , Ultra Low Density Polyethylene Resin |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | ATTANE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | OS9PfM_ATTANE-SL-4102G.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ATTANE™SL 4102G ultra-low density linear polyethylene copolymer is an ethylene-octene copolymer. This product is specially used for the production of blown film. It requires good processing performance, excellent sealing performance, thermal adhesion and toughness, and has excellent optical properties. Application field:
Meet the following regulatory requirements:
|
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity 1 | 0.905 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.0 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness 2(Shore D) | 40 | DIN 53505 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 40 | µm | |
| secant modulus | ASTM D882 | ||
| MD : 40 µm | 90.0 | MPa | ASTM D882 |
| TD : 40 µm | 95.0 | MPa | ASTM D882 |
| Tensile Stress | ISO 527-3 | ||
| MD : Yield, 40 µm | 5.70 | MPa | ISO 527-3 |
| TD : Yield, 40 µm | 5.40 | MPa | ISO 527-3 |
| MD : Break, 40 µm | 33.0 | MPa | ISO 527-3 |
| TD : Break, 40 µm | 30.0 | MPa | ISO 527-3 |
| Tensile Elongation | ISO 527-3 | ||
| MD : Break, 40 µm | 670 | % | ISO 527-3 |
| TD : Break, 40 µm | 790 | % | ISO 527-3 |
| Dart Drop Impact (40 µm) | > 850 | g | ISO 7765-1/B |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 40 µm | 660 | g | ASTM D1922 |
| TD : 40 µm | 800 | g | ASTM D1922 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature 3 | 84.0 | °C | ASTM D1525 |
| Melting Temperature | 122 | °C | DSC |
| Peak Crystallization Temperature (DSC) | 99.0 | °C | ISO 3146 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (20°, 40.0 µm) | 78 | ASTM D2457 | |
| Haze (40.0 µm) | 7.0 | % | ISO 14782 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 190 - 240 | °C |
| Extrusion instructions |
|---|
| 吹塑薄膜挤出的制造条件： 熔体温度：190 至 240°C（理想值：215-225°C） 放大比：1.5:1 至 3.5:1 建议的厚度范围：10 至 80 µm。 |
| Note Message | |
|---|---|
| 1 . | Compression molded sample |
| 2 . | Compression molded sample |
| 3 . | Compression molded sample |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Alpha PVC 2212RSM-100 CLEAR 000X | AlphaGary | PVC, Semi-Rigid | Alpha PVC |
| CALIBRE™ 200-10 | Trinseo | PC | CALIBRE™ |
| Petrotene® PP A3 C60 NTLA010 PH317 MSM | Petropol Industry and Trade of Polymers LTDA | PP Homopolymer | Petrotene® PP |
| Hifax TYC 2052P | LyondellBasell Industries | PP Copolymer | Hifax |
| Sylvin 9048-65 CLEAR | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |