DINALON® B1S25 G30 W
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Grupo Repol |
| Trademark: | DINALON® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ORwLrb_DINALON-B1S25-G30-W.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| DINALON®B1S25 G30 W is a polyamide 6 (nylon 6) product, which contains a 30% glass fiber reinforced material. It is available in Europe. The main characteristics are: moisture resistance. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.37 | g/cm³ | ISO 1183/A |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 9100 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 160 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.5 | % | ISO 527-2 |
| Flexural Modulus | 6500 | MPa | ISO 178 |
| Flexural Stress | 200 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 8.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 45 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 180 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 200 | °C | ISO 306/B |
| Additional Information |
|---|
| Humidity, Karl-Fisher, ISO 15512/A: <0.25%Vicat Softening Temperature, ISO 306, 50N: >200°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 9744-80FUV Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Wellamid® MR410 42H-NBK1 | Wellman Engineering Resins | Nylon 6 | Wellamid® |
| XENOY™ 6620U resin | SABIC Innovative Plastics | PC+PBT | XENOY™ |
| Aegis® H55ZP | Honeywell | Nylon 6 | Aegis® |
| PHOENIX™ 8901 | Phon Tech Industrial Company | TPE | PHOENIX™ |