CALIBRE™ 301-58 LT
| Category: | PC , Polycarbonate Resin |
| Manufacturer: | Trinseo |
| Trademark: | CALIBRE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | OQRg0C_CALIBRE-301-58-LT.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
CALIBRE™ 301-58 LT is a high light transmission, high-flow polycarbonate resin for injection molding applications. Main Characteristics:
Applications:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.20 | g/cm³ | ISO 1183/B |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 58 | g/10 min | ISO 1133 |
| Molding Shrinkage - Flow | 0.50 to 0.70 | % | ISO 294-4 |
| Water Absorption (23°C, 24 hr) | 0.20 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2300 | MPa | ISO 527-2/50 |
| Tensile Stress | ISO 527-2/50 | ||
| Yield | 60.0 | MPa | |
| Break | 48.0 | MPa | |
| Tensile Strain | ISO 527-2/50 | ||
| Yield | 6.0 | % | |
| Break | 60 | % | |
| Flexural Modulus 1 | 2500 | MPa | ISO 178 |
| Flexural Stress 2 | 100 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength (23°C) | 58 | kJ/m² | ISO 180/A |
| Unnotched Izod Impact Strength (23°C) | No Break | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Annealed | 137 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 124 | °C | ISO 75-2/A |
| 1.8 MPa, Annealed | 134 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 147 | °C | ISO 306/B50 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flammability Classification (0.750 mm) | V-2 | IEC 60695-11-10, -20 | |
| Glow Wire Flammability Index 3 | IEC 60695-2-12 | ||
| 1.00 mm | 850 | °C | |
| 2.00 mm | 900 | °C | |
| 3.00 mm | 960 | °C | |
| Glow Wire Ignition Temperature 4 | IEC 60695-2-13 | ||
| 1.00 mm | 875 | °C | |
| 2.00 mm | 875 | °C |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Refractive Index | 1.583 | ISO 489 | |
| Transmittance | > 90.0 | % | ASTM D1003 |
| Haze | < 1.0 | % | ASTM D1003 |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| 4 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| THERMOLAST® K TF4CGN (Series: FC) | KRAIBURG TPE | TPE | THERMOLAST® K |
| Fibremod™ GB306SAF | Borealis AG | PP, Unspecified | Fibremod™ |
| Formolene® HP5221 | Formosa Plastics Corporation, U.S.A. | HDPE | Formolene® |
| Huafon JF-P-6270 / JF-I-4118 | Huafon Group Co., Ltd. | PUR-Ester | Huafon |
| LUVOCOM® 1106-7743 VP | Lehmann & Voss & Co. | PEI | LUVOCOM® |