Generic Polyester Alloy
| Category: | Polyester Alloy , Polyester Alloy |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | OPt6k5_Generic-Polyester-Alloy.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic Polyester Alloy This information is provided for comparative purposes only. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.05 to 1.93 | g/cm³ | ASTM D792 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Barcol Hardness | 39 to 51 | ASTM D2583 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 2990 to 3890 | MPa | ASTM D638 |
| Tensile Strength | ASTM D638 | ||
| Yield, 23°C | 47.4 to 88.0 | MPa | |
| 23°C | 69.4 to 83.9 | MPa | |
| Tensile Elongation (Break, 23°C) | 2.3 to 4.0 | % | ASTM D638 |
| Flexural Modulus (23°C) | 2840 to 4250 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 110 to 141 | MPa | ASTM D790 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 74.9 to 143 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity (23°C) | 4.1E+13 to 5.5E+14 | ohms·cm | ASTM D257 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Mix Viscosity | 326 to 620 | cP | ASTM D2393 |
| Post Cure Time | 3.9 to 4.0 | hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Yuyao PA 033ML20 | Yuyao Tenglong Plastics Co., Ltd. | Nylon 66/6 | Yuyao PA |
| Cawiton® SN960 | Wittenburg B.V. | SEBS | Cawiton® |
| Fainplast PVC GK 75 | Fainplast Compounds S.r.l | PVC, Unspecified | Fainplast PVC |
| LACEA® H-100J (Unstretched) | Mitsui Chemicals, Inc. | PLA | LACEA® |
| ZEONEX® 790R | Zeon Corporation | COP | ZEONEX® |