TECHNYL® C 218L V30 Grey 3385 is a polyamide 6 reinforced with 30% glass fibre and UV stabilized for injection moulding. The product offers an excellent combination between thermal and mechanical properties.

General Information
Filler / Reinforcement	Glass fiber reinforced material, 30% filler by weight
Additive	heat stabilizer UV stabilizer
Features	Heat Stabilized - Inorganic Good dimensional stability Good UV resistance
Uses	Handle Application in Automobile Field
Appearance	Black Grey
Forms	Particle
Processing Method	Injection molding
Multi-Point Data	Isothermal Stress vs. Strain (ISO 11403-1)
Resin ID (ISO 1043)	PA6-GF30

Physical	Dry	Conditioned	Unit	Test Method
Density	1.35	--	g/cm³	ISO 1183/A
Water Absorption				ISO 62
23°C, 24 hr	1.7	--	%	ISO 62
Saturated, 23°C	6.1	--	%	ISO 62
Equilibrium, 23°C, 50% RH	2.2	--	%	ISO 62

Mechanical	Dry	Conditioned	Unit	Test Method
Tensile Modulus (23°C)	9300	6100	MPa	ISO 527-2/1A
Tensile Strength
Yield, 23°C	155	90.0	MPa	ASTM D638
Fracture, 23°C	160	--	MPa	ASTM D638
Fracture, 23°C	140	95.0	MPa	ISO 527-2/1A
Tensile Elongation
Fracture, 23°C	2.7	7.6	%	ASTM D638
Fracture, 23°C	2.7	7.5	%	ISO 527-2
Flexural Modulus
23°C	8500	--	MPa	ASTM D790
23°C	7700	5700	MPa	ISO 178
Flexural Strength
23°C	230	--	MPa	ASTM D790
23°C	210	155	MPa	ISO 178

Impact	Dry	Conditioned	Unit	Test Method
Charpy Notched Impact Strength (23°C)	8.0	13	kJ/m²	ISO 179/1eA
Charpy Unnotched Impact Strength (23°C)	55	75	kJ/m²	ISO 179/1eU
Notched Izod Impact
23°C	110	--	J/m	ASTM D256
23°C	8.0	15	kJ/m²	ISO 180
Unnotched Izod Impact (23°C)	65.0	85.0	kJ/m²	ASTM D256
Unnotched Izod Impact Strength (23°C)	65	70	kJ/m²	ISO 180/1U

Thermal	Dry	Conditioned	Unit	Test Method
Heat Deflection Temperature
0.45 MPa, not annealed	220	--	°C	ISO 75-2/Bf
1.8 MPa, not annealed	205	--	°C	ASTM D648
1.8 MPa, not annealed	202	--	°C	ISO 75-2/Af
Melting Temperature	222	--	°C	ISO 11357-3

Electrical	Dry	Conditioned	Unit	Test Method
Volume Resistivity	1.0E+15	1.0E+11	ohms·cm	IEC 60093
Dielectric Strength (2.00 mm)	--	22	kV/mm	IEC 60243-1
Relative Permittivity	3.80	4.50		IEC 60250
Comparative Tracking Index (Solution A)	550	475	V	IEC 60112

Flammability	Dry	Conditioned	Unit	Test Method
Flame Rating (3.2 mm)	HB	--		UL 94
Glow Wire Flammability Index (1.6 mm)	650	--	°C	IEC 60695-2-12
Oxygen Index	23	--	%	ISO 4589-2

Injection	Dry	Unit
Drying Temperature	80	°C
Suggested Max Moisture	0.20	%
Rear Temperature	230 - 235	°C
Middle Temperature	235 - 240	°C
Front Temperature	240 - 250	°C
Mold Temperature	60 - 90	°C

Injection instructions
The material is supplied in airtight bags, ready for use. In case that the virgin material has absorbed moisture, it must be dried with a dehumidified air drying equipment, dew point mini -20°C. Recommended time 2-4hInjection Advice: For reinforced polyamide, Solvay recommends the use of steel with a high content of Carbon and purified for polishing to avoid or limit the abrasion. For example: X38CrMoV5-1 (EN Norm) - 1.2367 /1.2343 (DIN Norm) or X160CrMoV12 (EN Norm) - 1.2601 /1.2379 (DIN Norm). For Mould Temperature, in the case of parts where the surface roughness is required we can recommend a temperature of 90°C to 120°C with an optimum at 105°C. The processing parameters like processing temperatures are a recommendation and can be adjusted in function of injection machine size, part geometry / design

Injection instructions

The material is supplied in airtight bags, ready for use. In case that the virgin material has absorbed moisture, it must be dried with a dehumidified air drying equipment, dew point mini -20°C. Recommended time 2-4hInjection Advice: For reinforced polyamide, Solvay recommends the use of steel with a high content of Carbon and purified for polishing to avoid or limit the abrasion. For example: X38CrMoV5-1 (EN Norm) - 1.2367 /1.2343 (DIN Norm) or X160CrMoV12 (EN Norm) - 1.2601 /1.2379 (DIN Norm). For Mould Temperature, in the case of parts where the surface roughness is required we can recommend a temperature of 90°C to 120°C with an optimum at 105°C. The processing parameters like processing temperatures are a recommendation and can be adjusted in function of injection machine size, part geometry / design

Category:	Nylon 6 , Polyamide 6
Manufacturer:	Solvay Engineering Plastics
Trademark:	TECHNYL®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	OPfVOX_TECHNYLC218LV30GREY3385.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
RABALON® SJ7400	Mitsubishi Chemical Performance Polymers, Inc.	TPE	RABALON®
Staramide RF005S	Eurostar Engineering Plastics	Nylon 66	Staramide
Vital-Line SHE4200	Teknor Apex Asia Pacific PTE. LTD.	PVC, Flexible	Vital-Line
ULTEM™ AR9100 resin	SABIC Innovative Plastics	PEI	ULTEM™
Chemlon® 204-13 GVNH BK083	Teknor Apex Company (Chem Polymer)	Nylon 6	Chemlon®