Xytron™ G4010T
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | DSM Engineering Plastics |
| Trademark: | Xytron™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | OOY6H2_XytronG4010T.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Xytron™G4010T is a polyphenylene sulfide (PPS) material, which contains a 40% glass fiber reinforced material. This product is available in North America, Europe or Asia Pacific,. Xytron™The main characteristics of G4010T are: flame retardant/rated flame. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.65 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Transverse flow | 0.50 | % | ISO 294-4 |
| Flow | 0.20 | % | ISO 294-4 |
| Water Absorption (Saturation, 23°C) | 0.020 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | ISO 2039-2 | ||
| M scale | 100 | ISO 2039-2 | |
| R scale | 121 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | ISO 527-2 | ||
| -- | 15000 | MPa | ISO 527-2 |
| 120°C | 7300 | MPa | ISO 527-2 |
| 160°C | 5200 | MPa | ISO 527-2 |
| 200°C | 3400 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | ||
| Fracture | 200 | MPa | ISO 527-2 |
| Fracture, 120°C | 105 | MPa | ISO 527-2 |
| Fracture, 160°C | 73.0 | MPa | ISO 527-2 |
| Fracture, 200°C | 55.0 | MPa | ISO 527-2 |
| Tensile Strain | ISO 527-2 | ||
| Fracture | 2.0 | % | ISO 527-2 |
| Fracture, 120°C | 3.1 | % | ISO 527-2 |
| Fracture, 160°C | 3.9 | % | ISO 527-2 |
| Fracture, 200°C | 6.4 | % | ISO 527-2 |
| Flexural Modulus | ISO 178 | ||
| -- | 14500 | MPa | ISO 178 |
| 120°C | 10000 | MPa | ISO 178 |
| 160°C | 5000 | MPa | ISO 178 |
| 200°C | 4200 | MPa | ISO 178 |
| Flexural Stress | 300 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 11 | kJ/m² | ISO 179/1eA |
| 23°C | 11 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 57 | kJ/m² | ISO 179/1eU |
| 23°C | 56 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact (23°C) | 11 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength (23°C) | 48 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 260 | °C | ISO 75-2/A |
| Melting Temperature 1 | 280 | °C | ISO 11357-3 |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow | 2.0E-5 | cm/cm/°C | ISO 11359-2 |
| Flow 2 | 2.5E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral | 4.0E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral 3 | 8.5E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric Strength | 22 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | 150 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flammability Classification | IEC 60695-11-10, -20 | ||
| 0.8 mm | V-0 | IEC 60695-11-10, -20 | |
| 1.5 mm | V-0 | IEC 60695-11-10, -20 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 - 120 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Rear Temperature | 300 - 320 | °C | |
| Middle Temperature | 310 - 330 | °C | |
| Front Temperature | 320 - 340 | °C | |
| Nozzle Temperature | 310 - 340 | °C | |
| Processing (Melt) Temp | 310 - 340 | °C | |
| Mold Temperature | 130 - 150 | °C | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 3.00 - 10.0 | MPa | |
| Screw Compression Ratio | 2.5:1.0 |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| 2 . | above Tg |
| 3 . | above Tg |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TORZEN® U4664FL BKB01 | INVISTA Engineering Polymers | Nylon 66 | TORZEN® |
| ACCUCOMP™ HP0315L | ACLO Compounders Inc. | PP Homopolymer | ACCUCOMP™ |
| Braskem PP CP350WV | Braskem America Inc. | PP Homopolymer | Braskem PP |
| EL-Pro™ P500J | SCG Chemicals Co., Ltd. | PP Homopolymer | EL-Pro™ |
| ISPLEN® PM 364 AT | REPSOL | PP Copolymer | ISPLEN® |