LEXAN™ CFR5630D resin
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics Asia Pacific |
| Trademark: | LEXAN™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | OOGYgl_LEXAN-CFR5630D-resin-87776.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LEXAN™ CFR5630D Polycarbonate (PC) is a non-filled resin, suitable for injection molding and extrusion. This non-chlorinated, non-brominated flame retardant PC resin meets FAR25.853 smoke density and 60 second vertical burn and OEM toxicity requirements. LEXAN CFR5630D resin is available in 5 prematched diffusion colors. |
| General Information | |
|---|---|
| Features |
|
| Agency Ratings |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.19 | g/cm³ | ASTM D792 |
| -- | 1.20 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 5.0 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (300°C/1.2 kg) | 5.00 | cm³/10min | ISO 1133 |
| Molding Shrinkage | Internal Method | ||
| Flow : 3.20 mm | 0.55 to 0.75 | % | |
| Across Flow : 3.20 mm | 0.60 to 0.80 | % | |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 0.14 | % | |
| Equilibrium, 23°C, 50% RH | 0.11 | % | |
| Outdoor Suitability | f1 | UL 746C |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2500 | MPa | ASTM D638 |
| -- | 2400 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 68.0 | MPa | ASTM D638 |
| Yield | 67.0 | MPa | ISO 527-2/50 |
| Break 3 | 52.0 | MPa | ASTM D638 |
| Break | 52.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 4 | 6.0 | % | ASTM D638 |
| Yield | 6.0 | % | ISO 527-2/50 |
| Break 5 | 51 | % | ASTM D638 |
| Break | 23 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 2400 | MPa | ASTM D790 |
| -- 7 | 2500 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 103 | MPa | ISO 178 |
| Yield, 50.0 mm Span 8 | 106 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9 | ISO 179/1eA | ||
| -30°C | 9.0 | kJ/m² | |
| 23°C | 10 | kJ/m² | |
| Charpy Unnotched Impact Strength 10 | ISO 179/1eU | ||
| -30°C | 130 | kJ/m² | |
| 23°C | 130 | kJ/m² | |
| Notched Izod Impact | |||
| -30°C | 85 | J/m | ASTM D256 |
| 23°C | 100 | J/m | ASTM D256 |
| -30°C 11 | 9.0 | kJ/m² | ISO 180/1A |
| 23°C 12 | 10 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | ASTM D4812, ISO 180/1U | ||
| -30°C | No Break | ||
| 23°C | No Break | ||
| Instrumented Dart Impact (23°C, Total Energy) | 66.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 131 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 100 mm Span 13 | 131 | °C | ISO 75-2/Be |
| 1.8 MPa, Unannealed, 3.20 mm | 120 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 100 mm Span 14 | 120 | °C | ISO 75-2/Ae |
| Vicat Softening Temperature | |||
| -- | 136 | °C | ASTM D1525 15 |
| -- | 137 | °C | ISO 306/B50 |
| -- | 139 | °C | ISO 306/B120 |
| Ball Pressure Test (125°C) | Pass | IEC 60695-10-2 | |
| CLTE | |||
| Flow : -40 to 40°C | 6.6E-5 | cm/cm/°C | ASTM E831 |
| Flow : 23 to 80°C | 7.2E-5 | cm/cm/°C | ISO 11359-2 |
| Transverse : -40 to 40°C | 7.0E-5 | cm/cm/°C | ASTM E831 |
| Transverse : 23 to 80°C | 7.6E-5 | cm/cm/°C | ISO 11359-2 |
| RTI Elec | 125 | °C | UL 746 |
| RTI Imp | 120 | °C | UL 746 |
| RTI Str | 125 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Constant (1.10 GHz) | 2.79 | ASTM ES7-83 | |
| Dissipation Factor (1.10 GHz) | 5.8E-3 | ASTM ES7-83 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glow Wire Flammability Index (1.00 mm) | 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature (1.00 mm) | 875 | °C | IEC 60695-2-13 |
| Oxygen Index | 45 | % | ISO 4589-2 |
| FAA Flammability 16 | PASSES | FAR 25.853 | |
| NBS Smoke Density - Flaming, Dmax | 70.0 | ASTM E662 | |
| Vertical Burn Test | FAR 25.853 | ||
| Test a (60 s), passes at | 5.0 | sec | |
| Test b (12 s), passes at | 5.0 | sec |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Drying Time, Maximum | 48 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 40 to 60 | % | |
| Rear Temperature | 266 to 288 | °C | |
| Middle Temperature | 277 to 299 | °C | |
| Front Temperature | 288 to 310 | °C | |
| Nozzle Temperature | 282 to 304 | °C | |
| Processing (Melt) Temp | 288 to 310 | °C | |
| Mold Temperature | 71.1 to 93.3 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 40 to 70 | rpm | |
| Vent Depth | 0.025 to 0.076 | mm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 50 mm/min |
| 3 . | Type I, 50 mm/min |
| 4 . | Type I, 50 mm/min |
| 5 . | Type I, 50 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*3 sp=62mm |
| 10 . | 80*10*3 sp=62mm |
| 11 . | 80*10*3 |
| 12 . | 80*10*3 |
| 13 . | 120*10*4 mm |
| 14 . | 120*10*4 mm |
| 15 . | Rate B (120°C/h), Loading 2 (50 N) |
| 16 . | Method A/B |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 4000 AR 10 TFE 10 SI 2 | RTP Company | PPA | RTP |
| ENFLEX VL-120-50D | Ravago Group | PP+EPDM | ENFLEX |
| Elvax® 3134SBZ | DuPont Packaging & Industrial Polymers | EVA | Elvax® |
| LubriOne™ AT-000/10T NATURAL | PolyOne Corporation | Acetal (POM) Copolymer | LubriOne™ |
| CP PRYME® Nylon 66 NN100LZ-7 | Chase Plastics Services Inc. | Nylon 66 | CP PRYME® Nylon 66 |