ENVIROPLAS® ENV08-NC610
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | ENVIROPLAS®, Inc. |
| Trademark: | ENVIROPLAS® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ON5fDg_ENVIROPLAS-ENV08-NC610.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Injection Molding Grade, Natural, Good Chemical/Solvent/Fuel/Oil Resistance, Good Wear and Weather Resistance, High Heat Resistance, Good Moldability |
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.31 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (250°C/2.16 kg) | 38 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.12 to 0.18 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 55.2 | MPa | ASTM D638 |
| Flexural Modulus | 2450 | MPa | ASTM D790 |
| Flexural Strength | 82.7 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 37 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 155 | °C | |
| 1.8 MPa, Unannealed | 60.0 | °C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (3.00 mm) | HB | Internal Method |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 85.0 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Rear Temperature | 229 to 254 | °C | |
| Middle Temperature | 229 to 254 | °C | |
| Front Temperature | 229 to 254 | °C | |
| Nozzle Temperature | 243 to 254 | °C | |
| Mold Temperature | 65.6 to 87.8 | °C | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 0.00 to 0.345 | MPa | |
| Screw Speed | 60 to 120 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP EMI 663 | RTP Company | ABS | RTP |
| SABIC® PPcompound 57F9722 | Saudi Basic Industries Corporation (SABIC) | PP Copolymer | SABIC® PPcompound |
| Next Nylon 6 Prime Series NX-01NC | Next Polymers Ltd. | Nylon 6 | Next Nylon 6 Prime Series |
| CERTENE™ HWB-1249 | Muehlstein | HDPE, EHMW | CERTENE™ |
| Fortron® ICE 714A | Celanese Corporation | PPS | Fortron® |