EZPrene 9055A
| Category: | TPV , Thermoplastic Vulcanizate |
| Manufacturer: | ENPLAST Americas, a Ravago Group Company |
| Trademark: | EZPrene |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | OMgGEA_EZPrene-9055A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 55 Shore A TPE (Thermoplastic Vulcanizate). Available in black, natural or pre-colored for injection molding and extrusion applications. This soft, easy to color material is non-hygroscopic and offers excellent chemical resistance and physical properties. EZPrene is polyolefin based and is 100% recyclable. |
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.930 | g/cm³ | ASTM D792 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240 | ||
| Shaw A, 5 seconds, extruded | 54 | ASTM D2240 | |
| Shore A, 5 seconds, injection molding | 56 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (100% Strain) | 2.10 | MPa | ASTM D412 |
| Tensile Strength (Break) | 4.20 | MPa | ASTM D412 |
| Tensile Elongation (Break) | 510 | % | ASTM D412 |
| Tear Strength | 21.0 | kN/m | ASTM D624 |
| Compression Set | ASTM D395 | ||
| 23°C, 22 hr | 28 | % | ASTM D395 |
| 125°C, 70 hr | 41 | % | ASTM D395 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | -60.0 | °C | ASTM D746 |
| Dynamic Service Temperature | 130 | °C |
| Additional Information | Nominal Value | Test Method | |
|---|---|---|---|
| Ozone Resistance | Excellent | ASTM D1149 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 2.0 - 3.0 | hr | |
| Rear Temperature | 191 - 204 | °C | |
| Middle Temperature | 196 - 210 | °C | |
| Front Temperature | 196 - 210 | °C | |
| Nozzle Temperature | 210 - 221 | °C | |
| Processing (Melt) Temp | 199 - 221 | °C | |
| Mold Temperature | 23.9 - 51.7 | °C | |
| Injection Pressure | 5.17 - 8.96 | MPa | |
| Injection Rate | Fast | ||
| Screw Speed | 50 - 200 | rpm | |
| Clamp Tonnage | 2.8 - 4.8 | kN/cm² | |
| Cushion | 5.08 - 12.7 | mm |
| Injection instructions |
|---|
| Holding Time: 5 to 7 Sec.Cooling Time: 30 to 50 Sec. |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Hopper Temperature | 166 - 177 | °C | |
| Cylinder Zone 1 Temp. | 171 - 191 | °C | |
| Cylinder Zone 2 Temp. | 171 - 191 | °C | |
| Cylinder Zone 3 Temp. | 171 - 191 | °C | |
| Cylinder Zone 4 Temp. | 171 - 191 | °C | |
| Cylinder Zone 5 Temp. | 171 - 191 | °C | |
| Adapter Temperature | 191 - 210 | °C | |
| Melt Temperature | 191 - 199 | °C | |
| Die Temperature | 191 - 210 | °C |
| Extrusion instructions |
|---|
| Screw: L/D 24:1 minimumCompression Zone: 355 - 390°F (180 - 200°C)Metering Zone: 375 to 410°F (190 to 210°C)Screw Speed: 30 - 80 rpmScreen Pack: 20/40/60 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sarlink® TPE ML-1160B BLK X (PRELIMINARY DATA) | Teknor Apex Company | TPE | Sarlink® TPE |
| TOTAL Polypropylene PPH 4022 | TOTAL Refining & Chemicals | PP Homopolymer | TOTAL Polypropylene |
| Daelim Po1y® PP-160UV | DAELIM INDUSTRIAL CO., LTD. | PP Homopolymer | Daelim Po1y® |
| INEOS HDPE TC46-25 | INEOS Olefins & Polymers USA | HDPE Copolymer | INEOS HDPE |
| Sylvin 8940-95 Red 6272 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |