MonoSol® AF L711
| Category: | PVOH , Polyvinyl Alcohol |
| Manufacturer: | MonoSol, LLC |
| Trademark: | MonoSol® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | OKQsNY_MonoSol-AF-L711.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
MonoSol AF L711 is a PVOH based thermoplastic film, soluble in cold water and manufactured using MonoSol AF's proprietary blown film technology. MonoSol AF L711 is a grade of PVOH cold water-soluble packaging film engineered for flow wrapping and pleat wrapping of tablets. This film has excellent stiffness for ease of processing on flow wrapping and pleat wrapping equipment. Available thickness range is 20 micron (0.8 mil) to 60 micron (2.4 mil). |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | |
|---|---|---|---|
| Moisture Content (23°C) 1 | 7.1 | wt% | |
| Solubility 2 | |||
| Disintegration : 10°C, 35.0 µm | 12.0 | sec | |
| Disintegration : 24°C, 35.0 µm | 5.0 | sec | |
| Dissolution : 10°C, 35.0 µm | 120.0 | sec | |
| Dissolution : 24°C, 35.0 µm | 72.0 | sec |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Yield (35.0 µm) | 22.9 | m²/kg | ASTM D4321 |
| Film Thickness - Tested | 35 | µm | |
| Film Thickness - Recommended / Available | 20 µm to 60 µm | ||
| Secant Modulus | ASTM D882, ISO 527-3 | ||
| 10%, MD : 36 µm | 89.6 | MPa | |
| 100%, MD : 36 µm | 33.8 | MPa | |
| 10%, TD : 36 µm | 82.7 | MPa | |
| 100%, TD : 36 µm | 22.8 | MPa | |
| Tensile Strength | |||
| MD : Break, 36 µm | 45.5 | MPa | ASTM D882 |
| TD : Break, 36 µm | 43.4 | MPa | ASTM D882 |
| MD : 36 µm | 45.5 | MPa | ISO 527-3 |
| TD : 36 µm | 43.4 | MPa | ISO 527-3 |
| Tensile Elongation | ASTM D882, ISO 527-3 | ||
| MD : Break, 36 µm | 180 | % | |
| TD : Break, 36 µm | 230 | % | |
| Dart Drop Impact (36 µm) | 560 | g | ASTM D1709, DIN 53433 |
| Elmendorf Tear Strength | |||
| MD : 36 µm | 390 | g | ASTM D1922 |
| TD : 36 µm | 390 | g | ASTM D1922 |
| MD : 36 µm | 0.040 | N | ISO 6383-2 |
| TD : 36 µm | 0.040 | N | ISO 6383-2 |
| Note Message | |
|---|---|
| 1 . | 50%RH |
| 2 . | Distilled Water (MSTM 205) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 207 H HS MS 2 | RTP Company | Nylon 66 | RTP |
| RONFALIN® C C110 | A. Schulman Europe | PC+ABS | RONFALIN® C |
| 3M™ Dyneon™ PTFE Compound TF 8615 | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ PTFE Compound |
| Leona™ TR161 | Asahi Kasei Chemicals Corporation | Nylon 66 | Leona™ |
| TOTAL Polyethylene L 425 | TOTAL Refining & Chemicals | mPE | TOTAL Polyethylene |