LONGLITE® PMC T383J
| Category: | Phenolic , Phenolic |
| Manufacturer: | CCP Group |
| Trademark: | LONGLITE® PMC |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | OHr2Ol_LONGLITE-PMC-T383J.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PMC-T383J Black Modified Phenolic is a two-stage, general purpose molding material offering excellent mold process-ability and optimized Cure cycles. Typical applications include cookware handles and knobs, Houseware appliance parts, etc. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| UL File Number |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.43 | g/cm³ | ASTM D792, JIS K7112 |
| Molding Shrinkage | 1.3 | % | JIS K6915, ASTM D955 |
| Water Absorption | |||
| 24 hr | 0.40 | % | ASTM D570 |
| 23°C, 24 hr | 0.40 | % | JIS K6911 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 53.9 | MPa | ASTM D638, JIS K6911 |
| Flexural Strength | 88.3 | MPa | ASTM D790, JIS K7203 |
| Compressive Strength | 196 | MPa | ASTM D695, JIS K6911 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Impact Strength | |||
| -- | 3.43 | kJ/m² | ASTM D256 |
| -- | 3.43 | kJ/m² | JIS K7111 |
| Izod Impact | |||
| -- | 29.4 | J/m | ASTM D256 |
| -- | 29.4 | J/m | JIS K6911 |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Shelf Life | 12 | month |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 155 | °C | ASTM D648, JIS K7207 |
| RTI Elec | 150 | °C | UL 746 |
| RTI Imp | 150 | °C | UL 746 |
| RTI Str | 150 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+12 | ohms·cm | ASTM D257, JIS K6911 |
| Dielectric Strength | 9.0 | kV/mm | ASTM D149, JIS K6915 |
| Arc Resistance | PLC 6 | ASTM D495 | |
| Comparative Tracking Index (CTI) | PLC 4 | UL 746 | |
| Insulation Resistance | |||
| -- 1 | 1.0E+10 | ohms | ASTM D257 |
| -- 2 | 1.0E+10 | ohms | JIS K6915 |
| -- 3 | 1.0E+8 | ohms | ASTM D257 |
| -- 4 | 1.0E+8 | ohms | JIS K6915 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (6.00 mm) | V-0 | UL 94 |
| Note Message | |
|---|---|
| 1 . | (N) |
| 2 . | (N) |
| 3 . | (B) |
| 4 . | (B) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SEPAZ™ K140HF | Mando Advanced Materials Co., Ltd. | PPS | SEPAZ™ |
| SUSTARIN® C GF 25 | Röchling Sustaplast SE & Co. KG | Acetal (POM) Copolymer | SUSTARIN® |
| EMPILON® 665T | EMPILON | SEBS | EMPILON® |
| EMOPLEN® AR 1205 RT2 | EMAS Plastik San.Tic.AS. | PP, Unspecified | EMOPLEN® |
| Lumid® GP2200B(W) | LG Chem Ltd. | Nylon 66 | Lumid® |