NuSil MED-4128

Category:	Rubber , Rubber
Manufacturer:	NuSil Technology
Trademark:	NuSil
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	OGnouN_NuSil-MED-4128.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

Message
NuSil Technology's restricted materials may be considered for use in short-term implant applications, 29 days or less, or for external applications. HCRs can be used for extrusion of tubing and profiles (rod or ribbon), in calendared sheeting for die-cutting, or in compression or transfer molded parts such as balloons, gaskets or o-rings. HCRs are clay-like in the uncured state and when cured generally exhibit very high mechanical properties and low modulus. HCRs with a peroxide cure system have a long history in implant applications.The cure mechanism can be vinyl specific or non vinyl specific. Non vinyl specific peroxide catalysts are more commonly used with HCRs than vinyl specific peroxide catalysts. Comments: LOW TENSION SET, UNCATALYZED

Message

NuSil Technology's restricted materials may be considered for use in short-term implant applications, 29 days or less, or for external applications.

HCRs can be used for extrusion of tubing and profiles (rod or ribbon), in calendared sheeting for die-cutting, or in compression or transfer molded parts such as balloons, gaskets or o-rings. HCRs are clay-like in the uncured state and when cured generally exhibit very high mechanical properties and low modulus.

HCRs with a peroxide cure system have a long history in implant applications.The cure mechanism can be vinyl specific or non vinyl specific. Non vinyl specific peroxide catalysts are more commonly used with HCRs than vinyl specific peroxide catalysts.

Comments: LOW TENSION SET, UNCATALYZED

General Information
Uses	Washer Pipe fittings Balloon application Profile Medical/nursing supplies
Agency Ratings	USP Class VI
Processing Method	Extrusion Resin transfer molding Profile extrusion molding Compression molding Calendering

Mechanical	Nominal Value	Unit
Tensile Strength (200% Strain)	0.621	MPa

Thermoset	Nominal Value	Unit
Post Cure Time (200°C)	2.0	hr

Additional Information	Nominal Value	Unit
Cure System	Peroxide
Plasticity: 65 mils

Uncured Properties	Nominal Value	Unit
Density	1.11	g/cm³
Curing Time (116°C)	0.17	hr

Cured Properties	Nominal Value	Unit
Shore Hardness (Shore A)	25
Tensile Strength	7.14	MPa
Tensile Elongation at Break	800	%
Tear Strength	12.3	kN/m

Resin Grade	Manufacturer	Category	Trademark
SCANAMID 6 B32^E Q30	Polykemi AB	Nylon 6	SCANAMID 6
Wondel® A AM3	Nanjing Julong Engineering Plastics Co., LTD	Nylon 66	Wondel® A
Estane® 2103-90AE TPU	Lubrizol Advanced Materials, Inc.	TPU-Polyether	Estane®
OLEFISTA™ QX0238C	Mitsubishi Chemical Performance Polymers, Inc.	Elastomer, Specialty	OLEFISTA™
Hostacom TRC 411N G82732	LyondellBasell Industries	PP, Unspecified	Hostacom