Karina WHITE PVC COMPOUND 809-D10/121-C-AC-AS
| Category: | PVC, Unspecified , Polyvinyl Chloride |
| Manufacturer: | Karina Ind. e Com. de Plásticos Ltda |
| Trademark: | Karina |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | OGguta_Karina-WHITE-PVC-COMPOUND-809-D10-121-C-AC-AS.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| WEATHER RESISTANT PVC COMPOUND RECOMMENDED FOR EXTRUSION OF COAXIAL CABLES JACKETS FOR OUTDOOR APPLICATIONS. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density 1 | 1.33 to 1.39 | g/cm³ | IEC 60811-1-3 |
| Color | OK | ME 12 | |
| Color a | -1.58 to 0.0200 | ME 12 | |
| Color b | 0.190 to 1.79 | ME 12 | |
| Color L | 92.7 to 94.3 | ME 12 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Maximum Variation of Elongation | < 25 | % | IEC 60811-1-2 |
| Maximum Variation of Tensile Strength | < 25 | % | IEC 60811-1-2 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A, 15 sec) | 78 to 82 | NBR 7456 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | > 12.6 | MPa | IEC 60811-1-1 |
| Tensile Strain (Yield) | > 130 | % | IEC 60811-1-1 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 2 | > 12.6 | MPa | IEC 60811-1-2 |
| Tensile Elongation 3(Break) | > 130 | % | IEC 60811-1-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -40.0 | °C | ASTM D746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity 4 | > 1.0E+13 | ohms·cm | NBR 5403 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxygen Index | > 28 | % | NBR 6245 |
| Note Message | |
|---|---|
| 1 . | 24 hr |
| 2 . | Aged in Air for 168 hr at 100°C |
| 3 . | Aged in Air for 168 hr at 100°C |
| 4 . | 24 hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Vytaflex® 50 | Smooth-On, Inc | PUR, Unspecified | Vytaflex® |
| XANTAR® G8F 23 R | Mitsubishi Engineering-Plastics Corp | PC | XANTAR® |
| Ferro PP NPP00GC19NA | Ferro Corporation | PP Homopolymer | Ferro PP |
| Formolon® 690 | Formosa Plastics Corporation, U.S.A. | PVC Homopolymer | Formolon® |
| Plaslube® PA6/6 GF15 TL5 | Techmer Engineered Solutions | Nylon 66 | Plaslube® |