ADVANCENE™ EE-1802-BSB

Category:	LLDPE , Linear Low Density Polyethylene
Manufacturer:	ETHYDCO
Trademark:	ADVANCENE™
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	OGX5ZD_ADVANCENEEE1802BSB.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

ADVANCENE™ EE-1802-BSB is a part of a Butene LLDPE series designed for the Blown & Cast film process, offering high gloss and excellent draw down. Films made from ADVANCENE™ EE-1802-BSB resin have very good tensile and toughness properties.

Applications:

Agricultural Film.

Bag in Box.

Cast Film.

Blown Film.

Bread Bags.

Food Packaging.

Form Fill and Seal Packaging.

Freezer Film.

Garment Film.

General Packaging.

Industrial Packaging.

Institutional Can Liners.

Lamination Film.

Liners.

Mulch Films.

Multilayer Packaging Film.

Packaging Films.

Personal Care.

Produce Bags on a Roll.

Shoppers.

Trash Can Liners.

General Information
Additive	Anti-caking agent (3500 ppm) Sliding agent (1500 ppm)
Features	Highlight smoothness Anti-caking property Recyclable materials Good stripping Good toughness
Uses	Blown Film Packaging Films Laminate Lining Bags Multilayer film Industrial application cast film Agricultural application Food packaging
Processing Method	Blow film cast film

Physical	Nominal Value	Unit	Test Method
Specific Gravity	0.918	g/cm³	ASTM D792
Melt Mass-Flow Rate (MFR) (190°C/2.16 kg)	2.0	g/10 min	ASTM D1238, ISO 1133

Films	Nominal Value	Unit	Test Method
Film Thickness - Tested	25	µm
secant modulus			ASTM D882
1% secant, MD	190	MPa	ASTM D882
1% secant, TD	220	MPa	ASTM D882
Tensile Strength			ASTM D882
MD : Yield	11.0	MPa	ASTM D882
TD : Yield	10.0	MPa	ASTM D882
MD : Fracture	49.0	MPa	ASTM D882
TD : Fracture	29.0	MPa	ASTM D882
Tensile Elongation			ASTM D882
MD : Fracture	600	%	ASTM D882
TD : Fracture	800	%	ASTM D882
Dart Drop Impact	66	g	ASTM D1709A, ISO 7765-1
Elmendorf Tear Strength			ASTM D1922
MD	85	g	ASTM D1922
TD	400	g	ASTM D1922

Thermal	Nominal Value	Unit	Test Method
Peak Melting Temperature	121	°C	ASTM D3418, ISO 3146

Optical	Nominal Value	Unit	Test Method
Gloss (45°)	76		ASTM D2457
Haze	4.4	%	ASTM D1003

Additional Information
The film properties have been measured on 25.4 µm (1.0 mil) thick film (screw diameter = 75 mm, die gap = 2.5 mm, BUR = 2.5 and temperature setting of 200°C).Optical film properties have been measured on a 25.4 µm thick film (without antiblock) with addition of 10% LDPE at the same conditions

Resin Grade	Manufacturer	Category	Trademark
Moplen EP640S	PolyMirae	PP Copolymer	Moplen
TEREZ PA 10.10 7500 GF 30 ECO	TER HELL PLASTIC GMBH	Nylon 1010	TEREZ PA 10.10
Karina GRAY PVC COMPOUND 751-18/69-B-IS	Karina Ind. e Com. de Plásticos Ltda	PVC, Unspecified	Karina
Sylvin 9773-70 Grey 9609	Sylvin Technologies Incorporated	PVC, Unspecified	Sylvin
LNP™ THERMOCOMP™ MF002AS compound	SABIC Innovative Plastics	PP, Unspecified	LNP™ THERMOCOMP™