POLYFLAM® RIPP 4000 OSD K3014
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | A. Schulman Europe |
| Trademark: | POLYFLAM® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | OGQy6F_POLYFLAM-RIPP-4000-OSD-K3014.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Flame-retardant PP-Copolymer, halogenfree, optimized smoke density |
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.07 | g/cm³ | ISO 1183/A |
| Melt Volume-Flow Rate (MVR) (230°C/2.16 kg) | 4.00 | cm³/10min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2100 | MPa | ISO 527-2/1A/1 |
| Tensile Stress | ISO 527-2/1A/50 | ||
| Yield | 20.0 | MPa | ISO 527-2/1A/50 |
| Fracture | 15.0 | MPa | ISO 527-2/1A/50 |
| Tensile Strain (Yield) | 3.3 | % | ISO 527-2/1A/50 |
| Nominal Tensile Strain at Break | 50 | % | ISO 527-2/1A/50 |
| Flexural Modulus 1 | 2100 | MPa | ISO 178 |
| Flexural Stress 2 | ISO 178 | ||
| 3.5% strain | 35.0 | MPa | ISO 178 |
| 4.0% strain | 35.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 20 | kJ/m² | ISO 179/1eU |
| 23°C | No Break | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 60.0 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | 74.0 | °C | ISO 306/B50 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flammability Classification | IEC 60695-11-10, -20 | ||
| 0.800 mm | V-0 | IEC 60695-11-10, -20 | |
| 1.60 mm | V-0 | IEC 60695-11-10, -20 | |
| 3.20 mm | V-0 | IEC 60695-11-10, -20 | |
| Glow Wire Flammability Index | IEC 60695-2-12 | ||
| 0.750 mm | 960 | °C | IEC 60695-2-12 |
| 1.50 mm | 960 | °C | IEC 60695-2-12 |
| 3.00 mm | 960 | °C | IEC 60695-2-12 |
| Additional Information |
|---|
| 1.) Not for use in food contact applications2.) Not for use in medical or pharmaceutical applications |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 - 80.0 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Rear Temperature | 180 | °C | |
| Middle Temperature | 200 | °C | |
| Front Temperature | 210 | °C | |
| Nozzle Temperature | 220 | °C | |
| Processing (Melt) Temp | 180 - 220 | °C | |
| Mold Temperature | 40.0 - 80.0 | °C | |
| Injection Pressure | 80.0 - 120 | MPa | |
| Injection Rate | Slow-Moderate | ||
| Holding Pressure | 40.0 - 90.0 | MPa | |
| Back Pressure | 5.00 - 10.0 | MPa | |
| Cushion | < 5.00 | mm | |
| Screw Speed | mm/sec |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC X4272 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| Sylvin 6064 NATURAL | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Karina BEIGE PVC COMPOUND 900-08/16-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Mafill® CT 4102 | Ravago Group | PP Copolymer | Mafill® |
| POLYCOMPO PE 5100B | POLYCOMPO Co.,Ltd. | HDPE | POLYCOMPO PE |