AKROMID® A3 GF 60 natural (2424)
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | AKRO-PLASTIC GmbH |
| Trademark: | AKROMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | OEywAP_AKROMID-A3-GF-60-natural-2424-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
AKROMID® A3 GF 60 natural (2424) is a 60% glass fibre reinforced polyamide 6.6 with very high rigidity and strength and light inherent color Applications are mainly components in mechanical engineering and in the automotive industry |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.71 | -- | g/cm³ | ISO 1183 |
| Spiral Flow | 53.0 | -- | cm | Internal Method |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 0.80 | -- | % | |
| Flow | 0.40 | -- | % | |
| Water Absorption (Saturation, 23°C) | 3.2 to 3.7 | -- | % | ISO 62 |
| Humidity Absorption - 62% RH (70°C) | 1.0 to 1.2 | -- | % | ISO 1110 |
| Additional Information | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Reinforcement Content | 60 | -- | % | ISO 1172 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Ball Indentation Hardness (H 961/30) | 330 | -- | MPa | ISO 2039-1 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 20500 | 15800 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 260 | 190 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 2.0 | 2.5 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 19800 | -- | MPa | ISO 178 |
| Flexural Stress 2 | 400 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 19 | -- | kJ/m² | |
| 23°C | 19 | 22 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 97 | -- | kJ/m² | |
| 23°C | 100 | 110 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 260 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 260 | -- | °C | ISO 75-2/A |
| 8.0 MPa, Unannealed | 235 | -- | °C | ISO 75-2/C |
| Melting Temperature 3 | 262 | -- | °C | DIN EN 11357-1 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+12 | 1.0E+10 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+13 | 1.0E+10 | ohms·cm | IEC 60093 |
| Comparative Tracking Index (Solution A) | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Rate 4(1.00 mm) | < 100 | -- | mm/min | FMVSS 302 |
| Flame Rating (1.60 mm) | HB | -- | UL 94 | |
| Glow Wire Flammability Index (1.60 mm) | 650 | -- | °C | IEC 60695-2-12 |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 10 K/min, DSC |
| 4 . | >1 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Rhelon F2538H-01 | RheTech, Inc. | Nylon 66 | Rhelon |
| TROSIFOL® Sound Control | Kuraray Co., Ltd. | PVB | TROSIFOL® |
| AKROMID® B3 GF 15 1 natural (2461) | AKRO-PLASTIC GmbH | Nylon 6 | AKROMID® |
| Five Plus™ HPP20T | Noble Polymers | PP Homopolymer | Five Plus™ |
| ALTECH® PC ECO 2020/146 FR GF20 | ALBIS PLASTIC GmbH | PC | ALTECH® PC |