Ultradur® B 4040 G6 High Speed
| Category: | PBT+PET , Polybutylene Terephthalate + PET |
| Manufacturer: | BASF Corporation |
| Trademark: | Ultradur® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | OEgvg8_Ultradur-B-4040-G6-High-Speed.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Easy flowing Injection moulding grade with 30 % glass fibres for industrial parts, rigid, tough and dimensionally stable, for example for eg windshield wiper arms, printed circuit boards, housing, consoles, contact carriers, covers. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.56 | g/cm³ | ISO 1183 |
| Apparent Density | 0.70 to 0.80 | g/cm³ | |
| Melt Volume-Flow Rate (MVR) (275°C/2.16 kg) | 33.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 1.0 | % | |
| Flow | 0.31 | % | |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 0.40 | % | |
| Equilibrium, 23°C, 50% RH | 0.20 | % | |
| Viscosity Number 1 | 85.0 | cm³/g | ISO 307 |
| Mold Shrinkage 2 | |||
| free, longitudinal | 0.14 | % | |
| free, transverse | 0.88 | % |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Maximum Service Temperature - short cycle operation | 210 | °C |
| Additional Information | Nominal Value | Test Method | |
|---|---|---|---|
| Automotive Materials (> 1.00 mm) | Passed | FMVSS 302 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Screw Speed | < 250 | mm/sec |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 10500 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 140 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.1 | % | ISO 527-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 7.4 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 40 | kJ/m² | |
| 23°C | 48 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 220 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 200 | °C | ISO 75-2/A |
| Melting Temperature | 223 | °C | ISO 11357-3 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+13 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+16 | ohms·cm | IEC 60093 |
| Relative Permittivity | IEC 60250 | ||
| 100 Hz | 4.00 | ||
| 1 MHz | 3.80 | ||
| Dissipation Factor | IEC 60250 | ||
| 100 Hz | 1.6E-3 | ||
| 1 MHz | 0.017 | ||
| Comparative Tracking Index (Solution A) | 250 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flammability Classification (1.60 mm) | HB | IEC 60695-11-10, -20 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 120 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.040 | % | |
| Hopper Temperature | 80.0 | °C | |
| Rear Temperature | 260 | °C | |
| Middle Temperature | 265 | °C | |
| Front Temperature | 270 | °C | |
| Nozzle Temperature | 270 | °C | |
| Processing (Melt) Temp | 250 to 275 | °C | |
| Mold Temperature | 60.0 to 100 | °C |
| Note Message | |
|---|---|
| 1 . | solution 0,005 g/ml Phenole/1,2 Dichlorbenzol 1:1 |
| 2 . | plate with film gate 150*150*3 mm³ |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RheTech Thermoplastic Polyolefin FT4802-690UVA | RheTech, Inc. | Polyolefin, Unspecified | RheTech Thermoplastic Polyolefin |
| MonoSol® M8900 | MonoSol, LLC | PVOH | MonoSol® |
| Topolymer® 4001 | Dongguan Top Polymer Enterprise | TPEE | Topolymer® |
| UNITHENE® LH608 | USI Corporation | HDPE | UNITHENE® |
| Dryflex® 4097-002 | ELASTO | TPO (POE) | Dryflex® |