RTP 4004 A FR

Category: PPA , Polyphthalamide
Manufacturer: RTP Company
Trademark: RTP
Fillers: -
Ports: Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms FOB, CIF, DAP, DAT, DDP
PDF: OEYOpI_RTP-4004-A-FR.pdf
PRICE: ​Order Products​ email   sales@su-jiao.com
Wechat: WECHAT
Message
Glass Fiber - Flame Retardant
General Information
Filler / Reinforcement
  • Glass fiber reinforced material, 25% filler by weight
Features
  • Flame retardancy
RoHS Compliance
  • Contact manufacturer
Processing Method
  • Injection molding
PhysicalNominal ValueUnitTest Method
Specific Gravity 1.65g/cm³ASTM D792
Molding Shrinkage - Flow (3.20 mm)0.35 - 0.55%ASTM D955
Moisture Content 0.10%
Additional InformationNominal ValueUnit
Primary Additive 25%
MechanicalNominal ValueUnitTest Method
Tensile Modulus 11000MPaASTM D638
Tensile Strength 138MPaASTM D638
Tensile Elongation (Yield)1.0 - 2.0%ASTM D638
Flexural Modulus 10000MPaASTM D790
Flexural Strength 200MPaASTM D790
ImpactNominal ValueUnitTest Method
Notched Izod Impact (3.20 mm)59J/mASTM D256
Unnotched Izod Impact (3.20 mm)400J/mASTM D4812
ThermalNominal ValueUnitTest Method
Deflection Temperature Under Load (1.8 MPa, Unannealed)260°CASTM D648
FlammabilityNominal ValueTest Method
Flame Rating (0.800 mm, ** Values per RTP Company testing.)V-0UL 94
InjectionNominal ValueUnit
Drying Temperature 107°C
Drying Time 4.0 - 6.0hr
Dew Point -28.9°C
Processing (Melt) Temp 307 - 343°C
Mold Temperature 65.6 - 163°C
Injection Pressure 68.9 - 103MPa
Injection instructions
Desiccant Type Dryer Required.
Resin Grade Manufacturer Category Trademark
TEREZ PA 6.6 HT 7500 GF 50 TER HELL PLASTIC GMBH Nylon 66 TEREZ PA 6.6
Unichem 7284 Colorite Polymers PVC, Unspecified Unichem
Chemraz 584 Greene, Tweed & Co. Perfluoroelastomer Chemraz
Durepol® PBT A3 G20 NTLA010 BT308 Petropol Industry and Trade of Polymers LTDA PBT Durepol® PBT
LNP™ LUBRICOMP™ SCL36 compound SABIC Innovative Plastics Nylon 12 LNP™ LUBRICOMP™