MAJORIS FFR200 BEIGE 7605
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | AD majoris |
| Trademark: | MAJORIS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | OCzq93_MAJORIS-FFR200-BEIGE-7605.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
FFR 200 BEIGE 7605 is a halogen flame retardant compound with UL 94 V0, intended for injection moulding. It has good flow rate and very good process ability. The product is available in natural (FFR 200) but other colours can be supplied on request. APPLICATIONS FFR 200 BEIGE 7605 is intended for the injection moulding of electrical component. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.36 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 16 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2/50 | ||
| Yield | 27.0 | MPa | ISO 527-2/50 |
| Fracture | 26.0 | MPa | ISO 527-2/50 |
| Tensile Strain | ISO 527-2/50 | ||
| Yield | 3.0 | % | ISO 527-2/50 |
| Fracture | 7.0 | % | ISO 527-2/50 |
| Flexural Modulus - 1% Secant | 2650 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30°C | 1.4 | kJ/m² | ISO 179 |
| 23°C | 2.3 | kJ/m² | ISO 179 |
| Notched Izod Impact | ISO 180 | ||
| -30°C | 2.0 | kJ/m² | ISO 180 |
| 23°C | 2.3 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 127 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 71.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 142 | °C | ISO 306/A |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.60 mm | V-0 | UL 94 | |
| 3.20 mm | V-0 | UL 94 | |
| 2.00 mm | 5VA | UL 94 | |
| Glow Wire Flammability Index (2.00 mm) | 960 | °C | IEC 60695-2-12 |
| Oxygen Index | 28 | % | ISO 4589-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 210 - 240 | °C | |
| Mold Temperature | 30.0 - 50.0 | °C | |
| Injection Rate | Moderate |
| Injection instructions |
|---|
| Holding pressure: 50 to 70% of the injection pressure |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Moplen EP3307 | PolyMirae | TPO (POE) | Moplen |
| Fortron® 1120L4 | Celanese Corporation | PPS | Fortron® |
| Dynacom 304-G30 | Dynachem Co. Ltd. | Nylon 66 | Dynacom |
| K-Prene 7000 XL 50 | Technovinyl Polymers India Ltd. | TPV | K-Prene |
| SABIC® PC PC5800 resin | SABIC Innovative Plastics Asia Pacific | PC | SABIC® PC |