Aristech Acrysteel® IGP
| Category: | Acrylic, Unspecified , Acrylic |
| Manufacturer: | Aristech Acrylics LLC |
| Trademark: | Aristech |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | OCmOSb_Aristech-Acrysteel-IGP.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Aristech Acrylics LLC Acrysteel® IGP is a continuous cast impact acrylic sheet with solvent cementability. The following physical properties were determined using 0.125" (3.17 mm) thickness clear Aristech Acrylics LLC Acrysteel ® IGP acrylic sheet. Properties may vary somewhat on other thicknesses and/or colors translucent or opaque). |
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.17 | g/cm³ | ASTM D792 |
| Water Absorption (Equilibrium, 3.17 mm) | 0.30 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 80 | ASTM D785 | |
| Barcol Hardness | 40 | ASTM D2583 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (3.17 mm) | 2510 | MPa | ASTM D638 |
| Tensile Strength (3.17 mm) | 51.0 | MPa | ASTM D638 |
| Tensile Elongation (Break, 3.17 mm) | 10 | % | ASTM D638 |
| Flexural Modulus | 2620 | MPa | ASTM D790 |
| Flexural Strength | 93.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength | 58 | kJ/m² | ASTM D6110 |
| Notched Izod Impact | 43 | J/m | ASTM D256 |
| Instrumented Dart Impact (4.75 mm) | 21.7 | J | FTMS 406-M-1074 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 82.2 | °C | ASTM D648 |
| CLTE - Flow (3.17 mm) | 7.6E-5 | cm/cm/°C | ASTM D696 |
| Thermal Conductivity | 0.20 | W/m/K | Internal Method |
| Thermal Stability - 30 minutes @ 180°C | No Effect | ASTM D4802 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Hot Forming Temperature (3.17 mm) | 171 to 193 | °C | Internal Method |
| Odor | None |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Refractive Index | 1.490 | ASTM D542 | |
| Transmittance | 92.8 | % | ASTM D1003 |
| Haze 1(3180 µm) | 2.5 | % | ASTM D1003 |
| Yellowness Index | ASTM D1925 | ||
| 3.17 mm | 1.8 | YI | |
| 4.75 mm | 2.0 | YI | |
| 5.58 mm | 2.2 | YI |
| Note Message | |
|---|---|
| 1 . | 23.9°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRL PC/TP-GP2 | Polymer Resources Ltd. | PC+Polyester | PRL |
| Tenite™ Acetate 132E5231229 Clear, Trsp | Eastman Chemical Company | CA | Tenite™ Acetate |
| Vi-Chem PVC VNC80-30I-504125-AGC | Vi-Chem Corporation | PVC, Unspecified | Vi-Chem PVC |
| Cardia Biohybrid™ BL-F | Cardia Bioplastics™ | TPS+PE | Cardia Biohybrid™ |
| Extir® CM Galileo Europa 5 Gold | Versalis S.p.A. | PS (EPS) | Extir® |