Order Products : sales@su-jiao.com
POLYfill PP EIP12030RF
| Category: | PP+EPDM , Polypropylene + EPDM Rubber |
| Manufacturer: | Polykemi AB |
| Trademark: | POLYfill |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | OCVgzc_POLYfill-PP-EIP12030RF.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PP/EPDM Mineral reinforced |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.10 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 12 | g/10 min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 0.80 to 1.0 | % | |
| Flow | 0.80 to 1.0 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | 26.0 | MPa | ISO 527-2 |
| Tensile Strain | ISO 527-2 | ||
| Yield | 5.0 | % | |
| Break | 16 | % | |
| Flexural Modulus (23°C) | 2500 | MPa | ISO 178 |
| Flexural Stress | 45.0 | MPa | ISO 178 |
| Scratch Resistance - 10 N Fine Structure | < 3.50 | dL | ISO 1518/D65 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -20°C | 3.0 | kJ/m² | |
| 23°C | 11 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179 | ||
| -20°C | 24 | kJ/m² | |
| 23°C | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 1 | |||
| 0.45 MPa, Unannealed | 116 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 64.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 145 | °C | ISO 306/A50 |
| -- | 75.0 | °C | ISO 306/B50 |
| CLTE - Flow | 5.5E-5 to 7.5E-5 | cm/cm/°C | Internal Method |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glow Wire Ignition Temperature (2.00 mm) | 750 | °C | IEC 60695-2-13 |
| Note Message | |
|---|---|
| 1 . | 120°C/hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Bapolene® 213B | Bamberger Polymers, Inc. | LDPE | Bapolene® |
| Hostaform® C 9021 SW XAP² ™ LS | Celanese Corporation | Acetal (POM) Copolymer | Hostaform® |
| OP - PC - Lubricated 15 PTFE | Oxford Polymers | PC | OP - PC - Lubricated |
| PPR PA6605HS | Premier Plastic Resins, Inc. | Nylon 66 | PPR |
| RTP 699 X 138787 E Nat/Clear | RTP Company | ABS | RTP |