NOVADURAN® 5020
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | Mitsubishi Engineering-Plastics Corp |
| Trademark: | NOVADURAN® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | OBfZYx_NOVADURAN-5020.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| NOVADURAN® 5020 is a Polybutylene Terephthalate (PBT) material. It is available in Asia Pacific, Europe, or North America for extrusion or injection molding. |
| General Information | |
|---|---|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.31 | g/cm³ | ISO 1183 |
| Molding Shrinkage | |||
| Across Flow : 2.00 mm | 1.8 | % | |
| Flow : 2.00 mm | 1.9 | % | |
| Water Absorption (Saturation, 23°C) | 0.10 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2550 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 51.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 4.0 | % | ISO 527-2 |
| Nominal Tensile Strain at Break | > 200 | % | ISO 527-2 |
| Flexural Modulus | 2300 | MPa | ISO 178 |
| Flexural Stress | 76.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 5.0 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | No Break | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 155 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 65.0 | °C | ISO 75-2/A |
| Melting Temperature | 224 | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | ||
| Flow : -30 to 50°C | 1.0E-4 | cm/cm/°C | |
| Flow : -30 to 120°C | 1.4E-4 | cm/cm/°C | |
| Flow : 50 to 120°C | 1.7E-4 | cm/cm/°C | |
| Transverse : -30 to 50°C | 1.0E-4 | cm/cm/°C | |
| Transverse : -30 to 120°C | 1.2E-4 | cm/cm/°C | |
| Transverse : 50 to 120°C | 1.5E-4 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+14 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+16 | ohms·cm | IEC 60093 |
| Electric Strength | IEC 60243-1 | ||
| 1.00 mm | 22 | kV/mm | |
| 2.00 mm | 17 | kV/mm | |
| Relative Permittivity (1 MHz) | 3.20 | IEC 60250 | |
| Dissipation Factor (1 MHz) | 0.020 | IEC 60250 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 5.0 to 8.0 | hr | |
| Rear Temperature | 235 | °C | |
| Middle Temperature | 240 | °C | |
| Front Temperature | 250 | °C | |
| Nozzle Temperature | 245 | °C | |
| Mold Temperature | 60.0 to 80.0 | °C | |
| Injection Pressure | 20.0 to 150 | MPa | |
| Screw Speed | 80 to 150 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC P88023 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| RTP EMI 962 | RTP Company | PSU | RTP |
| UBE Nylon 5033 FDX57 | UBE Engineering Plastics, S.A. | Nylon 66/6 | UBE Nylon |
| Allen ABS Luran® 776/LXS | SEKISUI Polymer Innovations, LLC | ABS | Allen ABS |
| Polifor® C 25 TR/25 UV GRIGIO 7437 | SO.F.TER. SPA | PP Copolymer | Polifor® |