OP - PC - Filled 10GF
| Category: | PC , Polycarbonate |
| Manufacturer: | Oxford Polymers |
| Trademark: | OP - PC - Filled |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | OBZlUy_OP---PC---Filled-10GF.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| OP - PC - Filled 10GF is a Polycarbonate (PC) material filled with 10% glass fiber. It is available in North America for injection molding. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.28 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.35 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3100 | MPa | ASTM D638 |
| Tensile Strength (Break) | 55.2 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 7.0 | % | ASTM D638 |
| Flexural Modulus | 3100 | MPa | ASTM D790 |
| Flexural Strength | 103 | MPa | ASTM D790 |
| Compressive Strength | 96.5 | MPa | ASTM D695 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 120 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 146 | °C | |
| 1.8 MPa, Unannealed | 141 | °C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Rear Temperature | 282 to 293 | °C | |
| Middle Temperature | 282 to 293 | °C | |
| Front Temperature | 288 to 293 | °C | |
| Nozzle Temperature | 288 to 316 | °C | |
| Processing (Melt) Temp | 288 | °C | |
| Mold Temperature | 82.2 to 116 | °C | |
| Injection Pressure | 89.6 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 1302 TFE 20 | RTP Company | PPS | RTP |
| SCHULAMID® 6MV14FR4K1681 | A. Schulman Inc. | Nylon 6 | SCHULAMID® |
| ULTEM™ 2210EPR resin | SABIC Innovative Plastics | PEI | ULTEM™ |
| Duron FR 950 | ProPolymers Inc. | Nylon, Unspecified | Duron |
| Hifax TRC 432P | LyondellBasell Industries | PP Copolymer | Hifax |