Sindustris ABS LPI753G
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Sincerity Australia Pty Ltd. |
| Trademark: | Sindustris ABS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | OBF1lz_Sindustris-ABS-LPI753G.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Sindustris ABS LPI753G is an Acrylonitrile Butadiene Styrene (ABS) material. It is available in Asia Pacific for extrusion. Typical applications include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| UL File Number |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.04 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 8.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 0.40 to 0.70 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 110 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield, 3.20 mm) | 55.9 | MPa | ASTM D638 |
| Tensile Elongation | ASTM D638 | ||
| Yield, 81.3 mm 2 | > 5.0 | % | |
| Break, 3.20 mm 3 | 30 | % | |
| Flexural Modulus 4(3.20 mm) | 2750 | MPa | ASTM D790 |
| Flexural Strength 5(3.20 mm) | 88.3 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| 23°C, 3.20 mm | 260 | J/m | |
| 23°C, 6.40 mm | 240 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 6.40 mm | 92.0 | °C | |
| 1.8 MPa, Unannealed, 6.40 mm | 86.0 | °C | |
| Vicat Softening Temperature | 94.0 | °C | ASTM D1525 6 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 to 80.0 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.010 | % | |
| Melt Temperature | 200 to 250 | °C | |
| Die Temperature | 200 to 250 | °C |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 1300 mm/min |
| 3 . | 50 mm/min |
| 4 . | 15 mm/min |
| 5 . | 15 mm/min |
| 6 . | Rate A (50°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| AIE PBT 30G3 | Asia International Enterprise (Hong Kong) Limited | PBT | AIE PBT |
| HiFill® PA6/6 GF14 IM HS L BK | Techmer Engineered Solutions | Nylon 66 | HiFill® |
| Plexiglas® SG7 | Altuglas International of Arkema Inc. | Acrylic (PMMA) | Plexiglas® |
| TECHNYL® C 218L V30 BLACK-J | Solvay Engineering Plastics | Nylon 6 | TECHNYL® |
| Sylvin 9940-55 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |