GETILAN ATP/190 X1 3A
| Category: | XLPE , Crosslinked Polyethylene |
| Manufacturer: | Crosspolimeri S.p.A. |
| Trademark: | GETILAN |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | OAVe6G_GETILAN-ATP-190-X1-3A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
GETILAN is the trade-mark of our crosslinkable (SIOPLAS technology) polythene. GETILAN ATP/190 X1 3A is a high density antiflame chemically crosslinkable polythene with high temperature index and low HCL content. Suitable for automotive cables insulation. It is a conveniently grafted polythene able to react in presence of moisture and of catalyst. We normally suggest our catalyst type MAC/203 HS MAC/203 HSL (less reactive). REACTION BETWEEN GRAFTING AND CATALYST: These two polythene, separately stored, must be mixed before starting extrusion in the ratio: GRAFTING/CATALYST 96/4 Certify: SAE J1127/J1128,FIAT 7.Z8220 T3 -T3 S,ISO 6722 Class C,LV 112 |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.15 | g/cm³ | ISO 1183 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 60 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 19.0 | MPa | IEC 60811 |
| Tensile Elongation (Break) | 230 | % | IEC 60811 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Tensile Strength in Air (150°C, 168 hr) | < 20 | % | IEC 60811 |
| Change in Tensile Strain at Break in Air (150°C, 168 hr) | < 20 | % | IEC 60811 |
| Heat Aging (175°C) 1 | Pass |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Service Temperature | -40 - 125 | °C | |
| Thermoset 2 | IEC 60811 | ||
| 200°C | 40 | % | IEC 60811 |
| Residual : 200°C | -5.0 | % | IEC 60811 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Halogen Content | % | IEC 60754-1 | |
| Oxygen Index | 24 - 25 | % | ASTM D2863 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 150 | °C | |
| Cylinder Zone 2 Temp. | 170 | °C | |
| Cylinder Zone 3 Temp. | 190 | °C | |
| Cylinder Zone 4 Temp. | 200 | °C | |
| Cylinder Zone 5 Temp. | 220 | °C | |
| Die Temperature | 225 | °C |
| Extrusion instructions |
|---|
| CROSSLINKING:Crosslinking of the finished product is obtained by: Immersion of the bobbin into hot water at 85/90°C for two hours (up to 3 mm thickness). Steam treatment at 0.15 for bar 5/6 hours. Faster ambient curing is possible depending from the atmospheric conditions. |
| Note Message | |
|---|---|
| 1 . | 6 hr on mandrel |
| 2 . | 20 N/cm² |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC X4292 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| Moplen RP1085 | LyondellBasell Industries | PP Random Copolymer | Moplen |
| DENKA EVA TEX NA500 | Denka Company Limited | EVA | DENKA EVA TEX |
| Hifax TYC007P | LyondellBasell Industries | TPO (POE) | Hifax |
| DEXFLEX® 911-UV | LyondellBasell Industries | PP, Unspecified | DEXFLEX® |