Nycast CP
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Cast Nylons Ltd. |
| Trademark: | Nycast |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | O9wZyB_Nycast-CP.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Nycast®CP being highly resilient, with higher tensile elongation and impact strength than standard grades has proven itself in many applications requiring an extra degree of toughness. A copolymer of caprolactam and laurinlactam, NYCAST CP was originally developed specifically for use in ball valve seats in the oil and gas industry. This durable material provides an economical, high performance bridge between NYCAST 6 and NYCAST 12 formulations. NYCAST CP with its higher elongation, superior dimensional stability and safety yellow color has found itself a superior choice for wobbler box inserts and coupling boxes in the cold rolling steel industry and mandrels covers in paper tube manufacturing plants. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.10 to 1.13 | g/cm³ | ASTM D792 |
| Water Absorption | ASTM D570 | ||
| 24 hr | 0.50 to 0.60 | % | |
| Saturation | 4.0 to 5.0 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 100 to 115 | ASTM D785 | |
| Durometer Hardness (Shore D) | 75 to 81 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1650 to 2280 | MPa | ASTM D638 |
| Tensile Strength | 60.0 to 79.3 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 25 to 80 | % | ASTM D638 |
| Flexural Modulus | 1970 to 2650 | MPa | ASTM D790 |
| Flexural Strength | 103 to 138 | MPa | ASTM D790 |
| Compressive Modulus | 1380 to 2070 | MPa | ASTM D695 |
| Compressive Strength | 75.8 to 86.2 | MPa | ASTM D695 |
| Shear Strength | 52.4 to 62.1 | MPa | ASTM D732 |
| Coefficient of Friction (vs. Itself - Dynamic) | 0.22 | ASTM D1894 | |
| Deformation Under Load | 0.400 to 0.700 | % | ASTM D621 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 48 to 75 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 204 to 221 | °C | |
| 1.8 MPa, Unannealed | 93.3 to 204 | °C | |
| Continuous Use Temperature | 98.9 | °C | ASTM D794 |
| Melting Temperature | 204 to 216 | °C | |
| CLTE - Flow | 9.0E-5 | cm/cm/°C | ASTM D696 |
| Service Temperature - Intermittent | 149 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength | 20 to 24 | kV/mm | ASTM D149 |
| Dielectric Constant | ASTM D150 | ||
| 60 Hz | 3.70 | ||
| 1 kHz | 3.70 | ||
| 100 kHz | 3.70 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Marlex® HHM 5502-01ST | Chevron Phillips Chemical Company LLC | HDPE | Marlex® |
| Manner Flexible PVC V945 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| SWANCOR Epoxy 907 | SWANCOR IND. CO., LTD. | Epoxy | SWANCOR Epoxy |
| Hax™ CAT 111 | Fainplast Compounds S.r.l | Polyolefin, Unspecified | Hax™ |
| LNP™ STAT-KON™ Ultem_UC1200 compound | SABIC Innovative Plastics | PEI | LNP™ STAT-KON™ |