AKROMID® T4 GF 50 black (3661)
| Category: | PPA , Polyphthalamide |
| Manufacturer: | AKRO-PLASTIC GmbH |
| Trademark: | AKROMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | O7E54H_AKROMID-T4-GF-50-black-3661-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
AKROMID® T4 GF 50 black (3661) is a 50% glass fibre reinforced polyphthalamide with very high rigidity and strength, as well as high temperature and chemical resistance Applications are parts with tight dimensional tolerances even under high mechanical load. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.62 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 0.70 | % | |
| Flow | 0.20 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 18000 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 280 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 2.3 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 17700 | MPa | ISO 178 |
| Flexural Stress 2 | 400 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 13 | kJ/m² | |
| 23°C | 15 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 90 | kJ/m² | |
| 23°C | 95 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 260 | °C | ISO 75-2/A |
| Melting Temperature 3 | 295 | °C | DIN EN 11357-1 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate 4(1.00 mm) | < 100 | mm/min | FMVSS 302 |
| Flame Rating (0.800 mm) | HB | UL 94 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Reinforcement Content | 50 | % | ISO 1172 |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 10 K/min, DSC |
| 4 . | >1 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Wellamid® GF33-66 22LH-NBK1 | Wellman Engineering Resins | Nylon 66 | Wellamid® |
| Borealis PP HA507MO | Borealis AG | PP Homopolymer | Borealis PP |
| Comai 663-3 BL | Comai Ltda | LLDPE | Comai |
| Innothane® IE-3010 | Innovative Polymers, Inc. | TSU | Innothane® |
| Karina CLEAR PVC COMPOUND 65/228-D-IS-SD | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |