Hytrel® 3046 NC010
| Category: | TPC-ET , THERMOPLASTIC POLYESTER ELASTOMER |
| Manufacturer: | DuPont Performance Polymers |
| Trademark: | Hytrel® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | O75XUW_Hytrel3046NC010.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 30 Shore D High Performance Polyester Elastomer Developed for Injection Molding |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Part Marking Code (ISO 11469) |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.07 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 11 | g/10 min | ISO 1133 |
| shrinkage- Flow | 0.90 | % | ISO 294-4 |
| Water Absorption (Equilibrium, 23°C, 2.00 mm, 50% RH) | 0.20 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ISO 868 | ||
| Shaw D | 30 | ISO 868 | |
| Shaw D, 15 seconds | 25 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 24.0 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | ||
| Fracture | 20.0 | MPa | ISO 527-2 |
| 10% strain | 1.90 | MPa | ISO 527-2 |
| 50% strain | 3.20 | MPa | ISO 527-2 |
| Tensile Strain (Break) | > 300 | % | ISO 527-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -40°C | No Break | ISO 179/1eA | |
| -30°C | No Break | ISO 179/1eA | |
| 23°C | No Break | ISO 179/1eA | |
| Notched Izod Impact | ISO 180/1A | ||
| -30°C | No Break | ISO 180/1A | |
| 23°C | No Break | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature 1 | 170 | °C | ISO 11357-3 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate 2(1.00 mm) | 41 | mm/min | ISO 3795 |
| FMVSS Flammability | B | FMVSS 302 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Emission of Organic Compounds | 1.50 | µgC/g | VDA 277 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature, Optimum | 205 | °C | |
| Mold Temperature, Optimum | 30 | °C | |
| Drying Recommended | yes | ||
| Drying Temperature | 80 | °C | |
| Drying Time - Desiccant Dryer | 2.0 - 3.0 | hr | |
| Suggested Max Moisture | 0.080 | % | |
| Processing (Melt) Temp | 190 - 210 | °C | |
| Mold Temperature | 30 - 40 | °C |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| 2 . | FMVSS 302 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ACCUTECH™ HP0336G15M15CL | ACLO Compounders Inc. | PP Homopolymer | ACCUTECH™ |
| LEXAN™ XHT2143 resin | SABIC Innovative Plastics Asia Pacific | PC | LEXAN™ |
| SCHULAMID® 612 GF 33 HE | A. Schulman Europe | Nylon 612 | SCHULAMID® |
| Thermec N™ 4314R45H | Technical Polymers, LLC | PPA | Thermec N™ |
| CYCOLAC™ EX58 resin | SABIC Innovative Plastics | ABS | CYCOLAC™ |