SABIC® PP 578N
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | O71954_SABIC-PP-578N.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SABIC® PP 578N is a nucleated PP homopolymer grade. This grade allows for cost efficient processing on the basis of good flow behavior, short cycle times, and robust processing behaviour. Products made from SABIC® PP 578N typically have low warpage, high stiffness in combination with moderate impact strength at room temperature, and a high gloss. SABIC® PP 578N is typically used in domestic appliances and furniture, even as replacement for talcum or chalk filled compounds. The product mentioned herein is in particular not tested and therefore not validated for use in pharmaceutical/ medical applications. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| UL File Number |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.905 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 25 | g/10 min | ASTM D1238, ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 113 | ASTM D785 | |
| Shore Hardness (Shore D) | 72 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 1% Secant 1 | 2000 | MPa | ASTM D638 |
| -- | 1900 | MPa | ISO 527-2/1A/1 |
| Tensile Strength | |||
| Yield 2 | 38.0 | MPa | ASTM D638 |
| Yield | 38.0 | MPa | ISO 527-2/1A/50 |
| Tensile Elongation | |||
| Yield 3 | 8.0 | % | ASTM D638 |
| Yield | 8.0 | % | ISO 527-2/1A/50 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 4.0 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| 23°C | 25 | J/m | ASTM D256A |
| 23°C | 3.0 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 100 | °C | ASTM D648 |
| 0.45 MPa, Unannealed 4 | 95.0 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed | 65.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed 5 | 60.0 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 154 | °C | ASTM D1525, ISO 306/A 6 6 |
| -- | 99.0 | °C | ASTM D1525, ISO 306/B 7 7 |
| Note Message | |
|---|---|
| 1 . | 1.0 mm/min |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | testbar 80*10*4mm |
| 5 . | testbar 80*10*4mm |
| 6 . | Rate B (120°C/h), Loading 1 (10 N) |
| 7 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Surlyn® 2601B | DuPont Packaging & Industrial Polymers | Ionomer | Surlyn® |
| ACCUTECH™ HP0315V | ACLO Compounders Inc. | PP Homopolymer | ACCUTECH™ |
| Sylvin 9077-92 White 1434 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| PENTAMID B GV35 H2 RC S black | PENTAC Polymer GmbH | Nylon 6 | PENTAMID B |
| LEXAN™ 131 resin | SABIC Innovative Plastics | PC | LEXAN™ |