Order Products : sales@su-jiao.com
Novalloy-E E70
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Daicel Polymer Ltd. |
| Trademark: | Novalloy-E |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | O70zWB_Novalloy-E-E70.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Novalloy-E E70 is an Acrylonitrile Butadiene Styrene (ABS) material. It is available in Asia Pacific. Primary attribute of Novalloy-E E70: Flame Rated. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.24 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (240°C/5.0 kg) | 10 | g/10 min | ISO 1133 |
| Molding Shrinkage - Flow | 0.30 to 0.50 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 28.0 | MPa | ISO 527-2 |
| Flexural Modulus | 1500 | MPa | ISO 178 |
| Flexural Stress | 40.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 13 | kJ/m² | ISO 179/1eA |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 71.0 | °C | ISO 75-2/A |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 4.0E+9 | ohms | ASTM D257 |
| Volume Resistivity | 2.0E+8 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 90.0 | °C | |
| Drying Time | 4.0 to 5.0 | hr | |
| Rear Temperature | 180 to 200 | °C | |
| Middle Temperature | 210 to 220 | °C | |
| Front Temperature | 220 to 230 | °C | |
| Nozzle Temperature | 210 to 220 | °C | |
| Mold Temperature | 40.0 to 70.0 | °C | |
| Back Pressure | 10.0 to 20.0 | MPa | |
| Screw Speed | 60 to 90 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MARPOL® HDB 502 Phillips Process | Marco Polo International, Inc. | HDPE | MARPOL® |
| Niche PA66MI40N | Niche Polymer, LLC | Nylon 66 | Niche |
| Geon™ Vinyl Rigid Extrusion L7035 | PolyOne Corporation | PVC, Rigid | Geon™ Vinyl Rigid Extrusion |
| ESTOPLAST EP 4030GY99 | Ester Industries Ltd. | PBT | ESTOPLAST EP |
| Telcar® TL-3071-60A (PRELIMINARY DATA) | Teknor Apex Company | TPE | Telcar® |