Hifax TRC 779 XLD E BLACK
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Hifax |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | O5QBlq_Hifax-TRC-779-XLD-E-BLACK.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Hifax TRC 779 XLD E Black high melt flow, 1,700 MPa flexural modulus, paintable, mineral-filled thermoplastic elastomeric olefin (TEO) resin has an excellent balance of properties and processability. It was designed for use in multiple automotive exterior applications. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.970 | g/cm³ | ISO 1183/A |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 24 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield, 23°C) | 16.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield, 23°C) | 5.0 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 1700 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | ISO 180 | ||
| -30°C | 7.0 | kJ/m² | |
| 23°C | 45 | kJ/m² | |
| Multi-Axial Instrumented Impact Energy 1(-40°C, Ductile Failure) | 23.0 | J | ISO 6603-2 |
| Note Message | |
|---|---|
| 1 . | 2.2 m/sec |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RenPIM® VG 5287 Polyol/ 5287 Isocyanate | Huntsman Advanced Materials | PUR, Unspecified | RenPIM® |
| Moplen HP544T | LyondellBasell Industries | PP Homopolymer | Moplen |
| NEXUS PE LL02-942 | Nexus Resin Group, LLC. | LLDPE | NEXUS PE |
| Karina GRAY PVC COMPOUND 750-18/473-F-IS-BZ | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| OmniPro™ HPP 10M FR0 | OMNI Plastics, LLC | PP Homopolymer | OmniPro™ |