VICTREX® PEEK 450GL15

Category:	PEEK , Polyetheretherketone
Manufacturer:	Victrex plc
Trademark:	VICTREX® PEEK
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	O5FXxM_VICTREX-PEEK-450GL15.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

High performance thermoplastic material, 15% glass fibre reinforced PolyEtherEtherKetone (PEEK), semi crystalline, granules for injection moulding and extrusion, standard flow, FDA food contact compliant, colour natural/beige.

Applications for higher strength in a static system. Low coefficient of thermal expansion. Chemically resistant to aggressive environments, suitable for sterilization for medical and food contact applications.

General Information
Filler / Reinforcement	Glass fiber reinforced material, 15% filler by weight
Features	Semicrystallization High strength Good disinfection Good liquidity Good chemical resistance Compliance of Food Exposure
Uses	Non-specific food applications Medical/nursing supplies
Agency Ratings	FDA Food Exposure, Not Rated
Appearance	Beige Natural color
Forms	Particles
Processing Method	Extrusion Injection molding

Physical	Nominal Value	Unit	Test Method
Density ¹	1.38	g/cm³	ISO 1183
Spiral Flow	10.0	cm	Internal method
Molding Shrinkage ²			ISO 294-4
Vertical flow direction : 180°C	0.90	%	ISO 294-4
Flow direction : 180°C	0.50	%	ISO 294-4
Water Absorption			ISO 62
23°C, 24 hr, 3.20 mm	0.060	%	ISO 62
Balance, 23°C, 3.20mm, 50% RH	0.40	%	ISO 62

Hardness	Nominal Value	Unit	Test Method
Durometer Hardness (Shore D, 23°C)	86		ISO 868

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus (23°C)	7500	MPa	ISO 527-2
Tensile Stress			ISO 527-2
Fracture, 23°C	140	MPa	ISO 527-2
Fracture, 125°C	80.0	MPa	ISO 527-2
Fracture, 175°C	45.0	MPa	ISO 527-2
Fracture, 275°C	25.0	MPa	ISO 527-2
Tensile Strain (Break, 23°C)	4.0	%	ISO 527-2
Flexural Modulus (23°C)	7000	MPa	ISO 178
Flexural Stress (23°C)	240	MPa	ISO 178
Compressive Stress			ISO 604
23°C	200	MPa	ISO 604
120°C	130	MPa	ISO 604
200°C	40.0	MPa	ISO 604

Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength (23°C)	5.5	kJ/m²	ISO 179/1eA
Charpy Unnotched Impact Strength (23°C)	60	kJ/m²	ISO 179/1U
Notched Izod Impact (23°C)	6.0	kJ/m²	ISO 180/A
Unnotched Izod Impact Strength (23°C)	55	kJ/m²	ISO 180

Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature (1.8 MPa, Unannealed)	298	°C	ISO 75-2/Af
Glass Transition Temperature ³	143	°C	ISO 11357-2
Melting Temperature	343	°C	ISO 11357-3
Linear thermal expansion coefficient			ISO 11359-2
Flow : < 143°C	2.5E-5	cm/cm/°C	ISO 11359-2
Flow : > 143°C	3.0E-5	cm/cm/°C	ISO 11359-2
Lateral : < 143°C	5.0E-5	cm/cm/°C	ISO 11359-2
Lateral : > 143°C	1.3E-4	cm/cm/°C	ISO 11359-2
Specific Heat (23°C)	1700	J/kg/°C	DSC
Thermal Conductivity (23°C)	0.30	W/m/K	ISO 22007-4

Electrical	Nominal Value	Unit	Test Method
Volume Resistivity	1.0E+16	ohms·cm	IEC 60093
Dielectric Strength (2.00 mm)	24	kV/mm	IEC 60243-1
Dielectric Constant (23°C, 1 kHz)	3.10		IEC 60250
Dissipation Factor (23°C, 1 MHz)	5.0E-3		IEC 60250
Comparative Tracking Index	150	V	IEC 60112

Fill Analysis	Nominal Value	Unit	Test Method
Melt Viscosity (400°C)	450	Pa·s	ISO 11443

Injection	Nominal Value	Unit
Drying Temperature	120 - 150	°C
Drying Time	3.0 - 5.0	hr
Hopper Temperature	< 100	°C
Rear Temperature	360	°C
Middle Temperature	365 - 370	°C
Front Temperature	375	°C
Nozzle Temperature	380	°C
Mold Temperature	170 - 200	°C

Injection instructions
Runner: Die / nozzle >3mm, manifold >3.5mmGate: >2mm or 0.5 x part thickness

Note Message
1 .	Crystalline
2 .	380°C nozzle
3 .	Onset

Resin Grade	Manufacturer	Category	Trademark
elitel UE3660	UNITIKA Plastics Division	TPC-ET	elitel
Hifax TRC 790P	LyondellBasell Industries	TPO (POE)	Hifax
LNP™ THERMOCOMP™ AF003 compound	SABIC Innovative Plastics	ABS	LNP™ THERMOCOMP™
Hypro-G™ PP-RP2C	Entec Polymers	PP Random Copolymer	Hypro-G™
Monprene® SP-14966	Teknor Apex Company	TPE	Monprene®