LNP™ LUBRICOMP™ DL0049EF compound
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | O4YNE1_LNPLUBRICOMPDL0049EFcompound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP DL0049EF is a compound based on Polycarbonate resin containing PTFE, Flame Retardant. Added features of this material include: Internally Lubricated. Also known as: LNP* LUBRICOMP* Compound DL-4040 FR Product reorder name: DL0049EF |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.35 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hours | 0.50 - 0.70 | % | ASTM D955 |
| Transverse flow : 24 hours | 0.80 - 1.0 | % | ASTM D955 |
| Vertical flow direction : 24 hours | 0.85 | % | ISO 294-4 |
| Flow direction : 24 hours | 0.61 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2070 | MPa | ASTM D638 |
| -- | 2090 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield | 47.6 | MPa | ASTM D638 |
| Yield | 49.0 | MPa | ISO 527-2 |
| Fracture | 40.7 | MPa | ASTM D638 |
| Fracture | 43.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield | 5.2 | % | ASTM D638 |
| Yield | 5.4 | % | ISO 527-2 |
| Fracture | 23 | % | ASTM D638 |
| Fracture | 26 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 2070 | MPa | ASTM D790 |
| -- | 2200 | MPa | ISO 178 |
| Flexural Stress | 70.0 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| With self-dynamics | 0.32 | ASTM D3702 Modified | |
| With Self-Static | 0.19 | ASTM D3702 Modified | |
| Wear Factor - Washer | 8.00 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 120 | J/m | ASTM D256 |
| 23°C 2 | 10 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 1600 | J/m | ASTM D4812 |
| 23°C 3 | 120 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 32.0 | J | ASTM D3763 |
| -- | 26.3 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 3.20mm | 137 | °C | ASTM D648 |
| 0.45 MPa, unannealed, 64.0mm span 4 | 136 | °C | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 3.20mm | 124 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 5 | 126 | °C | ISO 75-2/Af |
| Linear thermal expansion coefficient | |||
| Flow : -40 to 40°C | 7.6E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Lateral : -40 to 40°C | 7.9E-5 | cm/cm/°C | ASTM E831 |
| Lateral : -40 to 40°C | 7.8E-5 | cm/cm/°C | ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 293 - 304 | °C | |
| Middle Temperature | 304 - 316 | °C | |
| Front Temperature | 310 - 321 | °C | |
| Processing (Melt) Temp | 299 - 316 | °C | |
| Mold Temperature | 82.2 - 110 | °C | |
| Back Pressure | 0.172 - 0.344 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| 5 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Topolymer® 5711-651M | Dongguan Top Polymer Enterprise | TPE | Topolymer® |
| Xuchuan XCW-8425DH | Xuchuan Chemical (Suzhou) Co., Ltd | PUR, Unspecified | Xuchuan |
| Unichem 8588 | Colorite Polymers | PVC, Unspecified | Unichem |
| FRAGOM PR/55 PP | Crosspolimeri S.p.A. | Polyolefin, Unspecified | FRAGOM |
| Generic Nylon 612 - Glass Bead | Generic | Nylon 612 | Generic |