Asaprene™ T-438
| Category: | SBS , Styrene Butadiene Styrene Block Copolymer |
| Manufacturer: | AKelastomers |
| Trademark: | Asaprene™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | O4BUIM_Asaprene-T-438.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Specifically developed for superior characteristics and performance in pressure-sensitive and other adhesives, marked by good processability through low viscosity and a high level of balanced characteristics. It is supplied in pellet form. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.940 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 25 | g/10 min | ISO 1133 |
| Styrene/Butadiene | 35/65 | % | Internal Method |
| Viscosity | Internal Method | ||
| 15% solution in toluene | 48 | mPa·s | |
| 25% solution in toluene | 470 | mPa·s |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore A, 23°C, 2.00 mm, Compression Molded) | 80 | ISO 7619 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress 1(300% Strain, 23°C, 2.00 mm) | 3.00 | MPa | ISO 37 |
| Tensile Stress 2(Break, 23°C, 2.00 mm) | 5.00 | MPa | ISO 37 |
| Tensile Elongation 3(Break, 23°C, 2.00 mm) | 1200 | % | ISO 37 |
| Note Message | |
|---|---|
| 1 . | Type 1A |
| 2 . | Type 1A |
| 3 . | Type 1A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 701 SI 2 | RTP Company | HDPE | RTP |
| Sup-tech T601 | Shanghai Suptech Engineering Plastics Co. Ltd. | PBT | Sup-tech |
| Petrotene® PP A3 T10 NTLA010 PH374 MSP | Petropol Industry and Trade of Polymers LTDA | PP Homopolymer | Petrotene® PP |
| Dow Corning® C6-180 | Dow Corning Corporation | Silicone | Dow Corning® |
| LNP™ KONDUIT™ OX11315 compound | SABIC Innovative Plastics Asia Pacific | PPS | LNP™ KONDUIT™ |