EnCom PPE-PS 211-64
| Category: | PPE+PS , Polyphenylene Ether + PS |
| Manufacturer: | EnCom, Inc. |
| Trademark: | EnCom |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | O3Bgix_EnCom-PPE-PS-211-64.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| High Flow, High Impact PPE / HIPS Alloy |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.06 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 0.50 to 0.70 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.10 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 0.0414 | MPa | ASTM D638 |
| Flexural Modulus | 1940 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 340 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 108 | °C | |
| 1.8 MPa, Unannealed | 99.4 | °C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 87.8 to 110 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Drying Time, Maximum | 7.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 40 to 75 | % | |
| Rear Temperature | 238 to 293 | °C | |
| Middle Temperature | 243 to 299 | °C | |
| Front Temperature | 254 to 304 | °C | |
| Nozzle Temperature | 271 to 304 | °C | |
| Processing (Melt) Temp | 271 to 299 | °C | |
| Mold Temperature | 65.6 to 104 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 20 to 100 | rpm | |
| Vent Depth | 0.038 to 0.076 | mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Haysite Plastics H1000 | Haysite Reinforced Plastics | Polyester, TS | Haysite Plastics |
| Hyosung Polyketone M230A | Hyosung Corporation | PK-Aliphatic | Hyosung Polyketone |
| TECACOMP® TPE TC white 3975V | Ensinger GmbH | TPE | TECACOMP® |
| Sylvin 4280-65UV Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| LNP™ THERMOCOMP™ EX93452 compound | SABIC Innovative Plastics | PEI | LNP™ THERMOCOMP™ |