TOTAL Polypropylene PPC 9612
| Category: | PP Impact Copolymer , Polypropylene Impact Copolymer |
| Manufacturer: | TOTAL Refining & Chemicals |
| Trademark: | TOTAL Polypropylene |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | O13TFY_TOTAL-Polypropylene-PPC-9612.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Polypropylene PPC 9612 S02 has been developed specifically for the injection moulding of crates and is characterized by a high Melt Flow Index of 20 g/10 min. It allows an optimization of the injection parameters as for example a reduction of the cycle time, while keeping the keys properties for crates, namely rigidity, impact (at cold temperature) and long term creep resistance. Other injection molding applications like pails, food packaging, lids could benefit from this outstanding properties combination. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.905 | g/cm³ | ISO 1183 |
| Apparent Density | 0.53 | g/cm³ | ISO 60 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 20 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 82 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1250 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 24.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 5.0 | % | ISO 527-2 |
| Flexural Modulus | 1200 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | ISO 180 | ||
| -20°C | 6.5 | kJ/m² | |
| 23°C | 12 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 90.0 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 48.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 140 | °C | ISO 306/A50 |
| -- | 70.0 | °C | ISO 306/B50 |
| Melting Temperature (DSC) | 165 | °C | ISO 3146 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MEGOLON™ HF 8110 LD NATURAL UV | AlphaGary | TP, Unspecified | MEGOLON™ |
| Sylvin 5145-80 CLEAR YELLOW 4112 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| AKROMID® B3 GM 10/20 1 black 950058 (1829) | AKRO-PLASTIC GmbH | Nylon 6 | AKROMID® |
| Chemical Resources ABS500 | Chemical Resources, Inc. | ABS | Chemical Resources |
| TECACOMP® PA66 CF10 black 9084 | Ensinger GmbH | Nylon 66 | TECACOMP® |