Plaslube® AC-80/TF/15
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | Techmer Engineered Solutions |
| Trademark: | Plaslube® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | O0W4IZ_Plaslube-AC-80-TF-15.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Plaslube®AC-80/TF/15 is a polyoxymethylene (POM) copolymer product,. It can be processed by injection molding and is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific. Typical application areas are: engineering/industrial accessories. Features include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.49 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 2.0 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.23 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break, 23°C) | 43.4 | MPa | ASTM D638 |
| Flexural Modulus (23°C) | 2140 | MPa | ASTM D790 |
| Flexural Strength (Break, 23°C) | 66.2 | MPa | ASTM D790 |
| Coefficient of Friction | ASTM D1894 | ||
| With steel-dynamic | 0.16 | ASTM D1894 | |
| With steel-static | 0.080 | ASTM D1894 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 48 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 102 | °C | ASTM D648 |
| CLTE - Flow | 2.5E-5 | cm/cm/°C | ASTM D696 |
| Additional Information |
|---|
| Coefficient of Friction, Static, Thrust washer, 40psi, ambient temp.: 0.08Coefficient of Friction, Dynamic, Thrust washer, 40psi, 50 ft/min, ambient temp.: 0.16Limiting PV, Thrust washer, 100 FPM, ambient temp.: 1.2E4 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 1.0 - 2.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 177 - 188 | °C | |
| Middle Temperature | 188 - 199 | °C | |
| Front Temperature | 182 - 193 | °C | |
| Nozzle Temperature | 177 - 188 | °C | |
| Processing (Melt) Temp | 188 - 204 | °C | |
| Mold Temperature | 76.7 - 93.3 | °C | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 0.345 - 0.689 | MPa |
| Injection instructions |
|---|
| Screw Speed: MediumRecommendations for Molding and Tool Conditions: Well ventedMoisture Content, as received: Product is packaged at 0.2% or less.Drying not normally required. Dry at 180°F for 1 to 2 hours if necessary. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRE-ELEC® PS 1324 | Premix Oy | PS Alloy | PRE-ELEC® |
| Tekulon FR 645 | TEKUMA Kunststoff GmbH | PC | Tekulon |
| Alpha PVC 2228C/FS-65S WHITE 4001 | AlphaGary | PVC, Unspecified | Alpha PVC |
| KetaSpire® KT-820SFP | Solvay Specialty Polymers | PEEK | KetaSpire® |
| LNP™ THERMOCOMP™ DF005 compound | SABIC Innovative Plastics | PC | LNP™ THERMOCOMP™ |