LOFEX® A31LL
| Category: | PET , Polyethylene Terephthalate |
| Manufacturer: | Lotte Chemical Corporation |
| Trademark: | LOFEX® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | NzZKCS_LOFEX-A31LL.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| LOFEX ® A31LL is Polyester film is optically clear and both sides urethane treated with enhances adhesion to UV ink and coatings. It can use by silicon release film, protection film, window film because it has excellent run, easy treatment by suitable product. It has excellent properties by tensile strength, proper elongation and the thermal contraction rate. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Forms |
|
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 50 µm | 196 | MPa | |
| MD : Yield, 75 µm | 196 | MPa | |
| MD : Yield, 100 µm | 196 | MPa | |
| TD : Yield, 50 µm | 235 | MPa | |
| TD : Yield, 75 µm | 216 | MPa | |
| TD : Yield, 100 µm | 216 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 50 µm | 160 | % | |
| MD : Break, 75 µm | 170 | % | |
| MD : Break, 100 µm | 170 | % | |
| TD : Break, 50 µm | 110 | % | |
| TD : Break, 75 µm | 120 | % | |
| TD : Break, 100 µm | 120 | % | |
| F5 | ASTM D882 | ||
| MD : 50.0 µm | 113 | MPa | |
| MD : 75.0 µm | 113 | MPa | |
| MD : 100.0 µm | 113 | MPa | |
| TD : 50.0 µm | 113 | MPa | |
| TD : 75.0 µm | 113 | MPa | |
| TD : 100.0 µm | 113 | MPa |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Shrinkage | Internal Method | ||
| MD, 30 min : 150°C, 50.0 µm | 1.0 | % | |
| MD, 30 min : 150°C, 75.0 µm | 1.0 | % | |
| MD, 30 min : 150°C, 100.0 µm | 1.0 | % | |
| TD, 30 min : 150°C, 50.0 µm | 0.50 | % | |
| TD, 30 min : 150°C, 75.0 µm | 0.50 | % | |
| TD, 30 min : 150°C, 100.0 µm | 0.50 | % | |
| Surface Treatment | Both sides (Urethane) |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gardner Gloss | ASTM D523 | ||
| 60°, 50.0 µm | 160 | ||
| 60°, 75.0 µm | 160 | ||
| 60°, 100 µm | 160 | ||
| Transmittance | ASTM D1003 | ||
| 50.0 µm | 89.0 | % | |
| 75.0 µm | 89.0 | % | |
| 100 µm | 89.0 | % | |
| Haze | ASTM D1003 | ||
| 50.0 µm | 1.1 | % | |
| 75.0 µm | 1.2 | % | |
| 100 µm | 1.3 | % |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SOLPLAST TH 8000C | UTEKSOL d.o.o. | SEBS+SBS | SOLPLAST TH |
| MTEGRITY™ PP Homopolymer PP210 | M. Holland Company | PP Homopolymer | MTEGRITY™ PP Homopolymer |
| En Chuan 6011WAL | En Chuan Chemical Industries Co,. Ltd. | Polyester, TS | En Chuan |
| INSULCAST® 3230 LV/INSULCURE 9 | ITW Polymers Coatings North America | Epoxy | INSULCAST® |
| Karina GREEN PVC COMPOUND -E 911D40/ 77-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |