POLYblend PC/ABS 85H
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | Polykemi AB |
| Trademark: | POLYblend |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | NzAk7K_POLYblend-PC-ABS-85H.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PC/ABS-blend |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.15 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (260°C/5.0 kg) | 25 | g/10 min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 0.50 to 0.70 | % | |
| Flow | 0.50 to 0.70 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | 63.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 8.0 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 2400 | MPa | ISO 178 |
| Flexural Stress | 95.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30°C | 19 | kJ/m² | |
| 23°C | 53 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179 | ||
| -30°C | No Break | ||
| 23°C | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 1 | |||
| 0.45 MPa, Unannealed | 125 | °C | ISO 75-2/B |
| 0.45 MPa, Annealed | 127 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 108 | °C | ISO 75-2/A |
| 1.8 MPa, Annealed | 113 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 139 | °C | ISO 306/A50 |
| -- | 130 | °C | ISO 306/B50 |
| Ball Pressure Test (125°C) | Pass | IEC 60695-10-2 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 | |
| Glow Wire Ignition Temperature (2.00 mm) | 750 | °C | IEC 60695-2-13 |
| Note Message | |
|---|---|
| 1 . | 120°C/hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® F7880 | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| EPO-TEK® 301-2 | Epoxy Technology Inc. | Epoxy | EPO-TEK® |
| Kingfa MAC-751 | Kingfa | PC+ABS | Kingfa |
| LUVOCOM® 1/CF/20/TF/15/SI/2 | Lehmann & Voss & Co. | Nylon 66 | LUVOCOM® |
| ESTOPLAST XU 150HG BB01 | Ester Industries Ltd. | Nylon 6 | ESTOPLAST XU |