Plaslube® POM HO GF13 TL10 UV
| Category: | Acetal (POM) Homopolymer , Acetal (POM) Homopolymer |
| Manufacturer: | Techmer Engineered Solutions |
| Trademark: | Plaslube® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | NyPvvV_Plaslube-POM-HO-GF13-TL10-UV.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Plaslube® POM HO GF13 TL10 UV is an Acetal (POM) Homopolymer product filled with glass fiber. It can be processed by injection molding and is available in North America. Characteristics include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.60 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 0.80 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.30 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 110 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 95.1 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 2.5 | % | ASTM D638 |
| Flexural Modulus | 5720 | MPa | ASTM D790 |
| Flexural Strength | 143 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 64 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 168 | °C | |
| 1.8 MPa, Unannealed | 160 | °C | |
| CLTE - Flow | 5.0E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+15 | ohms·cm | ASTM D257 |
| Dielectric Strength 1 | 18 | kV/mm | ASTM D149 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.57 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 93.3 | °C | |
| Drying Time | 2.0 to 3.0 | hr | |
| Rear Temperature | 193 to 218 | °C | |
| Middle Temperature | 193 to 218 | °C | |
| Front Temperature | 193 to 218 | °C | |
| Processing (Melt) Temp | 193 to 227 | °C | |
| Mold Temperature | 82.2 to 104 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | Method A (Short-Time) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 201 TFE 5 | RTP Company | Nylon 66 | RTP |
| Elastron® V V101.A60.N | Elastron USA, Inc. | TPV | Elastron® V |
| GLS Nylon 66 LKG36 | GLS Polymers Pvt. Ltd. | Nylon 66 | GLS Nylon 66 |
| Petrothene® YR92866 | LyondellBasell Industries | LDPE+EVA | Petrothene® |
| PERLER® O08U1000B10 | A.D. Compound S.p.A. | PP Copolymer | PERLER® |