Polifor® E 3 NATURALE
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | SO.F.TER. SPA |
| Trademark: | Polifor® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | NwdPtq_Polifor-E-3-NATURALE.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polypropylene copolymer |
| General Information | |
|---|---|
| Features |
|
| Agency Ratings |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.900 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 2.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage | 1.6 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus | 1000 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | No Break | ASTM D256 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.60 mm | HB | ||
| 3.20 mm | HB | ||
| Glow Wire Ignition Temperature | 650 | °C | IEC 60695-2-13 |
| Oxygen Index | 21 | % | ASTM D2863 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 180 | °C | |
| Middle Temperature | 210 | °C | |
| Front Temperature | 220 | °C | |
| Mold Temperature | 30.0 to 50.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 4099 X 128641 A | RTP Company | PPA | RTP |
| Resilience™ HC 8230 | PolyOne Corporation | PVC, Rigid | Resilience™ |
| StarFlex P 7180-1000 | STAR Thermoplastic Alloys & Rubbers, Inc. | TPE | Starflex |
| TOTAL Polystyrene Compound 856 | TOTAL Refining & Chemicals | PS (IRPS) | TOTAL Polystyrene |
| ALCOM® LD2 PC 1000 14050 GY1118-14 | ALBIS PLASTIC GmbH | PC | ALCOM® LD2 PC |