POLYfill PPC TS6020 E20
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | Polykemi AB |
| Trademark: | POLYfill |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | NwT7oC_POLYfill-PPC-TS6020-E20.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Mineral reinforced Elastomer modified |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.05 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 6.0 | g/10 min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 1.0 to 1.2 | % | |
| Flow | 1.0 to 1.2 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | 24.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 6.0 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 2000 | MPa | ISO 178 |
| Flexural Stress | 35.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 11 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | No Break | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 1(1.8 MPa, Unannealed) | 65.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 140 | °C | ISO 306/A50 |
| -- | 60.0 | °C | ISO 306/B50 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 |
| Note Message | |
|---|---|
| 1 . | 120°C/hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Clariant Nylon 6/6 PA-111CF30 | Clariant Corporation | Nylon 66 | Clariant Nylon 6/6 |
| HiFill® PBT 1226 | Techmer Engineered Solutions | PBT | HiFill® |
| Laprene® 83E29ZA50 | SO.F.TER. SPA | SEBS | Laprene® |
| LG PS 65IHE | LG Chem Ltd. | PS (HIPS) | LG PS |
| Moplen HP521M | PolyMirae | PP Homopolymer | Moplen |