WPP PP PPC6TF2UV-Black
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | Washington Penn Plastic Co. Inc. |
| Trademark: | WPP PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Nw5alS_WPP-PP-PPC6TF2UV-Black.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
WPP PP PPC6TF2UV-Black is a polypropylene copolymer (PP Copoly) product, which contains 20% talc filler. It is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific. WPP PPC6TF2UV-Black applications include the automotive industry and consumer goods. Features include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.04 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 17 | g/10 min | ASTM D1238, ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 53 | ASTM D785 | |
| Durometer Hardness (Shore D) | 66 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 19.0 | MPa | ISO 527-2/50 |
| Flexural Modulus 1 | 1600 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ISO 180 | ||
| -30°C | 4.0 | kJ/m² | ISO 180 |
| 23°C | 23 | kJ/m² | ISO 180 |
| Dart Drop Impact 2(23°C) | 36.2 | J | ASTM D5420 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 101 | °C | ISO 75-2/B |
| Additional Information |
|---|
| Tested at 23 ± 2°C (73.4 ± 3.6°F) and 50 ± 5% relative humidity unless otherwise noted. |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 100% Reliability |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TRANSMARE® BIO 35LANF30-0.101 | Transmare Compounding B.V. | PLA | TRANSMARE® BIO |
| ACCUTECH™ HP0336C40L | ACLO Compounders Inc. | PP Homopolymer | ACCUTECH™ |
| Cellophane™ 335WSZB | Innovia Films Ltd. | Cellulose, Regenerated | Cellophane™ |
| FHR Polypropylene P6C6B-134 | Flint Hills Resources, LP | PP Impact Copolymer | FHR Polypropylene |
| Karina WHITE PVC COMPOUND -E 838-10/182-Y-ERYB | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |