Fortron® ICE 504L
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | Celanese Corporation |
| Trademark: | Fortron® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | NuzIqI_Fortron-ICE-504L.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| FORTRON ICE 504L is a 40% glass fiber reinforced material that belongs to our new generation of PPS. This new technology allows you to optimize your molding conditions with faster cycle times for complex shapes or process with low mold temperatures. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.65 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Vertical flow direction | 0.40 - 0.60 | % | ISO 294-4 |
| Flow direction | 0.20 - 0.60 | % | ISO 294-4 |
| Water Absorption (Saturation, 23°C) | 0.020 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 100 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 14700 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Break) | 195 | MPa | ISO 527-2/1A/5 |
| Tensile Strain (Break) | 1.9 | % | ISO 527-2/1A/5 |
| Flexural Modulus (23°C) | 14500 | MPa | ISO 178 |
| Flexural Stress | 285 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 10 | kJ/m² | ISO 179/1eA |
| 23°C | 10 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 53 | kJ/m² | ISO 179/1eU |
| 23°C | 53 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact | ISO 180/1A | ||
| -30°C | 10 | kJ/m² | ISO 180/1A |
| 23°C | 10 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength (23°C) | 34 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 1.8 MPa, not annealed | 270 | °C | ISO 75-2/A |
| 8.0 MPa, not annealed | 215 | °C | ISO 75-2/C |
| Glass Transition Temperature 1 | 90.0 | °C | ISO 11357-2 |
| Melting Temperature 2 | 280 | °C | ISO 11357-3 |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow | 2.6E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral | 4.2E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric Strength | 28 | kV/mm | IEC 60243-1 |
| Relative Permittivity (1 MHz) | 4.60 | IEC 60250 | |
| Dissipation Factor (1 MHz) | 6.2E-3 | IEC 60250 | |
| Comparative Tracking Index | 125 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.380 mm | V-0 | UL 94 | |
| 1.50 mm | V-0 | UL 94 | |
| Oxygen Index | 47 | % | ISO 4589-2 |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Specific Heat | 1500 | J/kg/°C | Internal method |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 130 - 140 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Hopper Temperature | 20.0 - 30.0 | °C | |
| Rear Temperature | 290 - 300 | °C | |
| Middle Temperature | 310 - 320 | °C | |
| Front Temperature | 330 - 340 | °C | |
| Nozzle Temperature | 310 - 330 | °C | |
| Processing (Melt) Temp | 330 - 340 | °C | |
| Mold Temperature | 90.0 - 160 | °C | |
| Injection Pressure | 50.0 - 100 | MPa | |
| Injection Rate | Fast | ||
| Holding Pressure | 30.0 - 70.0 | MPa | |
| Back Pressure | 0.00 - 3.00 | MPa |
| Injection instructions |
|---|
| Manifold Temperature: 330 to 340°CZone 4 Temperature: 330 to 340°CFeed Temperature: 60 to 80°C |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| 2 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Santoprene™ 201-73 | ExxonMobil Chemical | TPV | Santoprene™ |
| TAROLON 2500 W X0 | Taro Plast S.p.A. | PC | TAROLON |
| Complet® LGF50-PA66 MT | PlastiComp, Inc. | Nylon 66 | Complet® |
| Infino VB-5400G | SAMSUNG SDI CO., LTD. | PBT | Infino |
| Innoprene 1450N/B | Kumho Polychem Co., Ltd. | TPV | Innoprene |