SABIC® LDPE 2308AN00
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® LDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | NugG7S_SABIC-LDPE-2308AN00.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| SABIC®LDPE 2308AN00 is a low density polyethylene product,. It can be processed by film extrusion, blow molding, extrusion coating or injection molding, and is available in Europe. SABIC®LDPE 2308AN00 applications include foam and food contact applications. The main characteristics are: high liquidity. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.924 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 190°C/2.16 kg | 7.5 | g/10 min | ISO 1133 |
| 190°C/5.0 kg | 27 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) | ISO 1133 | ||
| 190°C/2.16 kg | 9.80 | cm³/10min | ISO 1133 |
| 190°C/5.0 kg | 35.0 | cm³/10min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, 15 sec, Compression Molded) | 47 | ISO 868 | |
| Ball Indentation Hardness (H 49/30) | 19.0 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (2.00 mm, Compression Molded) | 225 | MPa | ISO 527-2/1BA/50 |
| Tensile Stress | ISO 527-2/1BA/50 | ||
| Yield, 2.00mm, molded | 10.0 | MPa | ISO 527-2/1BA/50 |
| Fracture, 2.00mm, molded | 12.0 | MPa | ISO 527-2/1BA/50 |
| Tensile Strain (Break, 2.00 mm, Compression Molded) | 700 | % | ISO 527-2/1BA/50 |
| Tensile Creep Modulus | ISO 899-1 | ||
| 1 hr | 105 | MPa | ISO 899-1 |
| 1000 hr | 69.0 | MPa | ISO 899-1 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 5.5 50 | kJ/m² | ISO 180/1A |
| Tensile Impact Strength | 100 | kJ/m² | ISO 8256/1B |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 41.0 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 94.0 | °C | ISO 306/A50 |
| Additional Information |
|---|
| Modulus of Elasticity, SABIC Method: 300 MPaMelting Point, SABIC Method, DSC: 109°CCrystallization Temperature, SABIC Method, DSC: 98°CAverage Heat of Fusion, SABIC Method, DSC: 115 J/gESCR, SABIC Method, Determined in Rhodacal-DS10 at 60°C, 2 N/mm², thickness 3mm: 40hrTensile Impact Elongation at Break, ISO 8256, Type 1, Method B: 8.4%Tensile Impact Maximum Tension, ISO 8256, Type 1, Method B: 19 MPaMelting Point, DIN 53765, Tmelt(top) at 5°C/min: 109°CEnthalpy Change, DIN 53765: 115J/g |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Taitacell EPS 321F | Taita Chemical Company, Ltd. | PS (EPS) | Taitacell |
| ACCUCOMP™ SAN900L | ACLO Compounders Inc. | SAN | ACCUCOMP™ |
| ESTOPLAST EP 2030 | Ester Industries Ltd. | PBT | ESTOPLAST EP |
| Dynaprene® VE0064A | Nantex Industry Co., Ltd. | TPE | Dynaprene® |
| LNP™ THERMOCOMP™ EC006AQW compound | SABIC Innovative Plastics | PEI | LNP™ THERMOCOMP™ |